PPO PX9406-701 SABIC INNOVATIVE US
NORYL™
Household appliances、Household appliances、Automotive interior parts、Electronic communication 、Electronic communication
Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/PX9406-701 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 1100 J/m |
| Dart impact | 23°C, Energy at Peak | ASTM D3763 | 42.0 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/PX9406-701 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 18 % |
| 屈服 | ASTM D638 | 9.5 % | |
| tensile strength | 断裂 | ASTM D638 | 55.0 Mpa |
| bending strength | 屈服, 100 mm 跨距 | ASTM D790 | 111 Mpa |
| tensile strength | 屈服 | ASTM D638 | 75.0 Mpa |
| Flexural modulus | 100 mm 跨距 | ASTM D790 | 2640 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/PX9406-701 |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 2.0E+16 ohms·cm | |
| Surface Resistivity | ASTM D257 | > 1.0E+16 ohms | |
| Dissipation Factor | 50 Hz | ASTM D150 | 5.2E-3 |
| dielectric constant | 1 MHz | ASTM D150 | 2.49 |
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 2 | |
| High arc combustion index (HAI) | UL 746 | PLC 0 | |
| dielectric strength | 3.20 mm, in Oil | ASTM D149 | 19 KV/mm |
| dielectric constant | 60 Hz | ASTM D150 | 2.57 |
| Dissipation Factor | 60 Hz | ASTM D150 | 5.2E-3 |
| Hot wire ignition (HWI) | UL 746 | PLC 0 | |
| arc resistance | ASTM D495 | PLC 6 | |
| High Voltage Arc Traceability Rate (HVTR) | UL 746 | PLC 4 | |
| Dissipation Factor | 1 MHz | ASTM D150 | 2.6E-3 |
| dielectric constant | 50 kHz | ASTM D150 | 2.57 |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/PX9406-701 |
|---|---|---|---|
| UL flame retardant rating | 0.76 mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/PX9406-701 |
|---|---|---|---|
| Shrinkage rate | 横向流动 2 | 内部方法 | 0.50 - 0.70 % |
| Outdoor applicability | UL 746C | f2 | |
| Water absorption rate | 24 hr | ASTM D570 | 0.060 % |
| Shrinkage rate | 流动 : 3.20 mm | 内部方法 | 0.50 - 0.70 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/PX9406-701 |
|---|---|---|---|
| vicat | ASTM D15255 | 150 °C | |
| Heat distortion temperature | 1.8 MPa, 未退火, 6.40 mm，HDT | ASTM D648 | 122 °C |
| RTI Imp | UL 746 | 105 °C | |
| RTI | UL 746 | 110 °C | |
| Heat distortion temperature | 0.45 MPa, 未退火, 6.40 mm，HDT | ASTM D648 | 133 °C |
| RTI Elec | UL 746 | 110 °C |
| injection | Test Condition | Test Method | SABIC INNOVATIVE US/PX9406-701 |
|---|---|---|---|
| screw speed | 20 to 100 rpm | ||
| Suggested maximum moisture content | 0.020 % | ||
| Processing (melt) temperature | 275 to 305 °C | ||
| drying temperature | 105 to 110 °C | ||
| Suggested injection volume | 30 to 70 % | ||
| drying time | 3.0 to 4.0 hr | ||
| Temperature in the middle of the barrel | 255 to 300 °C | ||
| Temperature at the rear of the barrel | 245 to 295 °C | ||
| Exhaust hole depth | 0.038 to 0.051 mm | ||
| Temperature at the front of the material cylinder | 265 to 305 °C | ||
| Back pressure | 0.300 to 0.700 Mpa | ||
| Temperature | 70 to 100 °C | ||
| Spray nozzle temperature | 275 to 305 °C |