Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PP 1128NK SABIC SAUDI
SABIC®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Supplementary Information | Test Condition | Test Method | SABIC SAUDI/1128NK |
|---|---|---|---|
| tear strength | MD:50.0µm | DIN 53455 | 42.0 Mpa |
| TD:50.0µm | DIN 53455 | 38.0 Mpa |
| hardness | Test Condition | Test Method | SABIC SAUDI/1128NK |
|---|---|---|---|
| ball-indentation hardness | H358/30 | ISO 2039-1 | 76.0 Mpa |
| film | Test Condition | Test Method | SABIC SAUDI/1128NK |
|---|---|---|---|
| Dart impact | 50µm,铸造薄膜 | ASTM D1709 | 280 g |
| elongation | MD:断裂,50µm,铸造薄膜 | DIN 53455 | 680 % |
| film thickness | 50 µm | ||
| elongation | TD:断裂,50µm,铸造薄膜 | DIN 53455 | 720 % |
| Mechanical properties | Test Condition | Test Method | SABIC SAUDI/1128NK |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 1500 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 35.0 Mpa |
| Flexural modulus | 横向流量:0.0500mm,铸造薄膜 | DIN 53121 | 670 Mpa |
| 流量:0.0500mm,铸造薄膜 | DIN 53121 | 700 Mpa | |
| coefficient of friction | DIN 53375 | 0.18 | |
| Tensile strain | 断裂 | ISO 527-2/50 | >50 % |
| 屈服 | ISO 527-2/50 | 9.0 % |
| optical performance | Test Condition | Test Method | SABIC SAUDI/1128NK |
|---|---|---|---|
| Haze ratio | 1000µm,注塑 | ASTM D1003 | 2.7 % |
| gloss | 20°,50.0µm,铸造薄膜 | ISO 2813 | 100 |
| physical property | Test Condition | Test Method | SABIC SAUDI/1128NK |
|---|---|---|---|
| melt mass-flow rate | 230°C/2.16kg | ISO 1133 | 11 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC SAUDI/1128NK |
|---|---|---|---|
| vicat | ISO 306/A50 | 154 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 85.0 °C |
| melting temperature | ISO 3146 | 163 °C |