PA66 Matrixx F663E23 USA The Matrixx Group
--
--
Filler, glass fiber reinforced material, 23%, filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | USA The Matrixx Group/Matrixx F663E23 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C,3.18mm | ASTM D256 | 64 J/m |
| Supplementary Information | Test Condition | Test Method | USA The Matrixx Group/Matrixx F663E23 |
|---|---|---|---|
| ReinforcementContent | ASTM D5630 | 23 % |
| Mechanical properties | Test Condition | Test Method | USA The Matrixx Group/Matrixx F663E23 |
|---|---|---|---|
| Flexural modulus | 23°C,3.18mm | ASTM D790 | 6620 MPa |
| tensile strength | 屈服,23°C,3.18mm | ASTM D638 | 148 MPa |
| flammability | Test Condition | Test Method | USA The Matrixx Group/Matrixx F663E23 |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| physical property | Test Condition | Test Method | USA The Matrixx Group/Matrixx F663E23 |
|---|---|---|---|
| Shrinkage rate | MD | 内部方法 | 0.20to0.50 % |
| density | ASTM D792 | 1.29 g/cm³ |
| Thermal performance | Test Condition | Test Method | USA The Matrixx Group/Matrixx F663E23 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,3.18mm，HDT | ASTM D648 | 243 °C |
| RTI Imp | UL 746 | 65.0 °C | |
| RTI Str | UL 746 | 65.0 °C | |
| RTI Elec | UL 746 | 65.0 °C |