Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT D202 SHINKONG TAIWAN
SHINITE®
Bottle cap、Electronic field、Electrical field
Glass fiber reinforced、Flame retardant
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SHINKONG TAIWAN/D202 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 3.17mm | ASTMD256 | 27 J/m |
| hardness | Test Condition | Test Method | SHINKONG TAIWAN/D202 |
|---|---|---|---|
| Rockwell hardness | R级 | ASTMD785 | 118 |
| Mechanical properties | Test Condition | Test Method | SHINKONG TAIWAN/D202 |
|---|---|---|---|
| elongation | 断裂 | ASTMD638 | 6.0 % |
| tensile strength | ASTMD638 | 61.4 Mpa | |
| compressive strength | ASTMD695 | 100 Mpa | |
| Flexural modulus | ASTMD790 | 2760 Mpa | |
| Tensile modulus | ASTMD638 | 3310 Mpa | |
| bending strength | ASTMD790 | 93.8 Mpa |
| Electrical performance | Test Condition | Test Method | SHINKONG TAIWAN/D202 |
|---|---|---|---|
| Volume resistivity | ASTMD257 | 1E+16 ohms·cm | |
| dielectric strength | ASTMD149 | 19 KV/mm | |
| dielectric constant | ASTMD150 | 3.00 |
| flammability | Test Condition | Test Method | SHINKONG TAIWAN/D202 |
|---|---|---|---|
| UL flame retardant rating | UL94 | V-0 |
| physical property | Test Condition | Test Method | SHINKONG TAIWAN/D202 |
|---|---|---|---|
| density | ASTMD792 | 1.42 g/cm³ | |
| Water absorption rate | 23°C,24hr | ASTMD570 | 0.080 % |
| Shrinkage rate | MD | ASTMD955 | 2.0to2.2 % |
| Thermal performance | Test Condition | Test Method | SHINKONG TAIWAN/D202 |
|---|---|---|---|
| MD | ASTMD696 | 9E-05 cm/cm/°C | |
| melting temperature | DSC | 224 °C | |
| 1.8MPa,未退火 | ASTMD648 | 60.0 °C |