PA66/PTFE RL-4030 HS NAT SABIC INNOVATIVE US
LNP™ LUBRICOMP™
Electronic and electrical、Automotive components、Casters
High temperature resistan、resist fatigue
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/RL-4030 HS NAT |
|---|---|---|---|
| Suspended wall beam notch impact strength 6 | 23°C | ISO180/1A | 3.0 kJ/m² |
| Unscented Izod Impact Strength 6 | 23°C | ISO180/1U | 15 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/RL-4030 HS NAT |
|---|---|---|---|
| Tensile stress | 断裂 | ISO527-2/5 | 51.0 Mpa |
| Bending stress 2 | --4 | ISO178 | 83.0 Mpa |
| Tensile modulus | ISO527-2/1 | 3100 Mpa | |
| Fracture bending strain 5 | ISO178 | 4.5 % | |
| Tensile strain | 断裂 | ISO527-2/5 | 2.7 % |
| Bending stress 2 | --3 | ISO178 | 82.0 Mpa |
| Bending modulus 2 | ISO178 | 2700 Mpa |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/RL-4030 HS NAT |
|---|---|---|---|
| UL flame retardant rating | 3.0mm,TestingbySABIC | UL94 | V-0 |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/RL-4030 HS NAT |
|---|---|---|---|
| Shrinkage rate | MD | 内部方法 | 1.3 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/RL-4030 HS NAT |
|---|---|---|---|
| Hot deformation temperature 7 | 0.45MPa,未退火,64.0mm跨距 | ISO75-2/Bf | 149 °C |
| 1.8MPa,未退火,64.0mm跨距 | ISO75-2/Af | 89.0 °C | |
| MD：23到60°C | ISO11359-2 | 7.3E-05 cm/cm/°C |