Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPC LEXAN™ 4504 resin SABIC
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC/LEXAN™ 4504 resin |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 15 kJ/m² |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 73.0 J |
| Impact strength of cantilever beam gap | -30°C | ASTM D256 | 140 J/m |
| 23°C | ASTM D256 | 640 J/m | |
| -30°C | ISO 180/1A | 11 kJ/m² | |
| 23°C | ASTM D4812 | 3200 J/m | |
| 23°C | ISO 180/1A | 13 kJ/m² | |
| ASTM D1822 | 578 kJ/m² | ||
| Dart impact | 23°C | ASTM D3029 | 149 J |
| hardness | Test Condition | Test Method | SABIC/LEXAN™ 4504 resin |
|---|---|---|---|
| Rockwell hardness | M计秤 | ASTM D785 | 85 |
| R计秤 | ASTM D785 | 122 |
| Mechanical properties | Test Condition | Test Method | SABIC/LEXAN™ 4504 resin |
|---|---|---|---|
| tensile strength | 屈服 | ISO 527-2/5 | 65.0 MPa |
| elongation | 屈服 | ASTM D638 | 7.0 % |
| tensile strength | 屈服 | ASTM D638 | 65.5 MPa |
| Flexural modulus | ISO 178 | 2120 MPa | |
| Tensile strain | 屈服 | ISO 527-2/50 | 7.0 % |
| tensile strength | 屈服 | ISO 527-2/50 | 65.0 MPa |
| bending strength | ISO 178 | 66.0 MPa | |
| elongation | 断裂 | ASTM D638 | 120 % |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 95.1 MPa |
| Tensile modulus | ASTM D638 | 2090 MPa | |
| tensile strength | 断裂 | ASTM D638 | 71.7 MPa |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 2030 MPa |
| Tensile strain | 断裂 | ISO 527-2/50 | >50 % |
| Tensile modulus | ISO 527-2/1 | 2260 MPa |
| Electrical performance | Test Condition | Test Method | SABIC/LEXAN™ 4504 resin |
|---|---|---|---|
| dielectric strength | 3.20mm,inAir | ASTM D149 | 20 kV/mm |
| Dissipation Factor | 50Hz | ASTM D150 | 1.2E-03 |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 3 |
| Dissipation Factor | 60Hz | ASTM D150 | 1.2E-03 |
| dielectric constant | 60Hz | ASTM D150 | 3.15 |
| Dissipation Factor | 100Hz | ASTM D150 | 0.024 |
| Volume resistivity | ASTM D257 | >2.6E+17 ohms·cm | |
| dielectric constant | 50Hz | ASTM D150 | 3.15 |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 4 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 2 |
| dielectric constant | 1MHz | ASTM D150 | 3.00 |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 3 |
| optical performance | Test Condition | Test Method | SABIC/LEXAN™ 4504 resin |
|---|---|---|---|
| Haze ratio | 2540µm | ASTM D1003 | 1.0 % |
| refractive index | ASTM D542 | 1.600 | |
| transmissivity | 2540µm | ASTM D1003 | 85.0 % |
| flammability | Test Condition | Test Method | SABIC/LEXAN™ 4504 resin |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | V-2 |
| physical property | Test Condition | Test Method | SABIC/LEXAN™ 4504 resin |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.70to0.80 % |
| Water absorption rate | 24hr | ASTM D570 | 0.16 % |
| 平衡,23°C,50%RH | ISO 62 | 0.35 % | |
| 饱和,23°C | ISO 62 | 0.16 % | |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 3.00 cm³/10min |
| density | ASTM D792 | 1.19 g/cm³ | |
| Specific volume | ASTM D792 | 0.830 cm³/g | |
| density | ISO 1183 | 1.20 g/cm³ | |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 3.0 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC/LEXAN™ 4504 resin |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD：-40到40°C | ISO 11359-2 | 6E-05 cm/cm/°C |
| MD：-40到95°C | ASTME831 | 9.2E-05 cm/cm/°C | |
| vicat | ASTM D152511 | 160 °C | |
| Linear coefficient of thermal expansion | MD：-40到40°C | ISO 11359-2 | 6E-05 cm/cm/°C |
| RTI Str | UL 746 | 125 °C | |
| specific heat | ASTMC351 | 1260 J/kg/°C | |
| vicat | -- | ISO 306/B120 | 155 °C |
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 6E-05 cm/cm/°C |
| thermal conductivity | ASTMC177 | 0.21 W/m/K | |
| vicat | -- | ISO 306/B50 | 154 °C |
| Linear coefficient of thermal expansion | MD：-40to40°C | ASTME831 | 6E-05 cm/cm/°C |
| RTI Imp | UL 746 | 125 °C | |
| Heat distortion temperature | 1.8MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Af | 132 °C |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 143 °C | |
| RTI Elec | UL 746 | 125 °C |