Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC GS2020MR2 MITSUBISHI THAILAND
IUPILON™
fibre
enhance、Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Electrical performance | Test Condition | Test Method | MITSUBISHI THAILAND/GS2020MR2 |
|---|---|---|---|
| dielectric strength | ASTM D149 | 23 KV/mm | |
| dielectric constant | ASTM D150 | 3.05 |
| Mechanical properties | Test Condition | Test Method | MITSUBISHI THAILAND/GS2020MR2 |
|---|---|---|---|
| Flexural modulus | 6.40mm | ASTM D790 | 6350 Mpa |
| elongation | 断裂，3.20mm | ASTM D638 | 4.0 % |
| bending strength | 6.40mm | ASTM D790 | 185 Mpa |
| Impact strength of cantilever beam gap | 3.20mm | ASTM D256 | 140 J/m |
| Rockwell hardness | R计秤 | ASTM D785 | 124 |
| tensile strength | 3.20mm | ASTM D638 | 106 Mpa |
| physical property | Test Condition | Test Method | MITSUBISHI THAILAND/GS2020MR2 |
|---|---|---|---|
| Shrinkage rate | MD：3.00mm | ASTM D955 | 0.20-0.40 % |
| Water absorption rate | 24hr | ASTM D570 | 0.11 % |
| melt mass-flow rate | 300℃/1.2kg | ASTM D1238 | 10-12 g/10min |
| density | ASTM D792 | 1.33 g/cm³ |
| Thermal performance | Test Condition | Test Method | MITSUBISHI THAILAND/GS2020MR2 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 145 °C |
| UL flame retardant rating | 1.60mm | UL 94 | V-2 |
| Linear coefficient of thermal expansion | ASTM D696 | 0.000024 cm/cm/℃ |