Mechanical properties	Test Condition	Test Method	BASF GERMANY/1185A
Shore hardness		DIN 53505	87 shoreA
Tensile modulus	100%	DIN 53504-S2	6 N/mm
compression set	室温	DIN 53517	25 %
Tensile modulus	300%	ASTM D412/ISO 527	6 Mpa/Psi
		100%	ASTM D412/ISO 527	2.5 Mpa/Psi
		300%	DIN 53504-S2	10 N/mm
Impact strength of cantilever beam gap	＋23℃	DIN 53453	不破裂 KJ/m
tear strength		ASTM D624/ISO 34	70 n/mm²
tensile strength		DIN 53504-S2	45 N/mm
Impact strength of cantilever beam gap	－30℃	DIN 53453	不破裂 KJ/m
Shore hardness		ASTM D2240/ISO 868	36 Shore D
compression set	70℃	DIN 53517	45 %
tensile strength		ASTM D412/ISO 527	45 Mpa/Psi
Shore hardness		DIN 53505	36 Shore D
tensile strength	80℃水中21天	DIN 53504-S2	32 N/mm
Tensile modulus	20%	DIN 53504-S2	2.5 N/mm
elongation at break	80℃水中21天	DIN 53504-S2	600 %
Friction loss		DIN 53516	25 mm
Shore hardness		ASTM D2240/ISO 868	87 Shore A
elongation at break		DIN 53504-S2	600 %
tear strength		DIN 53515	70 N/mm

other	Test Condition	Test Method	BASF GERMANY/1185A
characteristic			用于射出、挤出、吹出