Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PP 1009 HS NATURAL POLYPACIFIC AUSTRALIA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | POLYPACIFIC AUSTRALIA/1009 HS NATURAL |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 3.00mm | ASTM D256 | 380 J/m |
| Impact strength of cantilever beam gap | 3.00mm | ASTM D256 | 26 J/m |
| hardness | Test Condition | Test Method | POLYPACIFIC AUSTRALIA/1009 HS NATURAL |
|---|---|---|---|
| Shore hardness | 邵氏D,15秒,3.00mm | ASTM D2240 | 70 |
| 邵氏D,3.00mm | ASTM D2240 | 77 | |
| Rockwell hardness | R级,3.00mm | ASTM D785 | 101 |
| Mechanical properties | Test Condition | Test Method | POLYPACIFIC AUSTRALIA/1009 HS NATURAL |
|---|---|---|---|
| tensile strength | 3.00mm | ASTM D638 | 33.0 MPa |
| elongation | 断裂,3.00mm | ASTM D638 | 30 % |
| Flexural modulus | 3.00mm | ASTM D790 | 2880 MPa |
| physical property | Test Condition | Test Method | POLYPACIFIC AUSTRALIA/1009 HS NATURAL |
|---|---|---|---|
| Shrinkage rate | MD：3.00mm | ASTM D955 | 1.1to1.3 % |
| melt mass-flow rate | 230°C/2.16kg | ASTM D1238 | 21 g/10min |
| density | ASTM D792 | 1.05 g/cm³ |
| Thermal performance | Test Condition | Test Method | POLYPACIFIC AUSTRALIA/1009 HS NATURAL |
|---|---|---|---|
| Linear coefficient of thermal expansion | MD：-30到30°C,3.00mm | ASTM D696 | 8E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,未退火,3.00mm，HDT | ASTM D648 | 128 °C |
| 1.8MPa,未退火,3.00mm，HDT | ASTM D648 | 72.0 °C |