ASA/PC TA-15 HB UMG JAPAN
UMG ALLOY®
--
High impact resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | UMG JAPAN/TA-15 HB |
|---|---|---|---|
| Tensile stress | 23 ℃，屈服 | ISO 527-2 | 51 Mpa |
| bending strength | 23 ℃ | ISO 178 | 86 Mpa |
| Flexural modulus | 23 ℃ | ISO 178 | 2450 Mpa |
| Tensile modulus | 23 ℃ | ISO 527-2 | 2100 Mpa |
| Charpy Notched Impact Strength | 23 ℃ | ISO 179 | 50 kJ/m² |
| physical property | Test Condition | Test Method | UMG JAPAN/TA-15 HB |
|---|---|---|---|
| Rockwell hardness | ISO 2039-2 | 106 Mpa | |
| Melt volume flow rate | 230℃/2.16kg | ISO 1133 | 9.00 cm3/10min |
| Shrinkage rate | 流量 | ISO 294-4 | 0.5-0.7 % |
| Thermal performance | Test Condition | Test Method | UMG JAPAN/TA-15 HB |
|---|---|---|---|
| Linear coefficient of thermal expansion | ISO 11359-2 | 0.000095 cm/cm/℃ | |
| Heat distortion temperature | 1.8MPa，HDT | ISO 75-2/A | 94 °C |