PC DX02437 SABIC INNOVATIVE US
LNP™ THERMOCOMP™
Automotive components、Electronic and electrical
Thermal stability、Low temperature resistanc、Filler: carbon powder
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/DX02437 |
|---|---|---|---|
| 1.8MPa, Unannealed,64.0mm Span | ISO75-2/Af | 126 °C | |
| 1.8MPa, Unannealed,3.20mm | ASTMD648 | 111 °C | |
| Vicat Softening Temperature | ISO306/A50,ASTMD152517 | 144 °C |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/DX02437 |
|---|---|---|---|
| Break | ASTMD638 | 47.0 Mpa | |
| fracture | ISO527-2/5 | 47.0 Mpa | |
| Flexural Modulus | ISO178 | 2550 Mpa | |
| ASTMD638 | 2570 Mpa | ||
| Break | ASTMD638 | 19 % | |
| yield | ISO527-2/5 | 58.0 Mpa | |
| Flexural Strain (Break) | ISO178 | 7.8 % | |
| fracture | ISO527-2/5 | 17 % | |
| Flexural Stress | --8 | ISO178 | 92.0 Mpa |
| --9 | ISO178 | 90.0 Mpa | |
| Yield | ASTMD638 | 58.0 Mpa |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/DX02437 |
|---|---|---|---|
| Modeling Shrinkage | MD | 内部方法 | 0.64 % |
| Melt Volume flow Rate | 300°C/5.0kg | ISO1133 | 16.0 cm3/10min |
| Modeling Shrinkage | TD | 内部方法 | 0.68 % |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/DX02437 |
|---|---|---|---|
| ASTMD3763 | 39.1 J | ||
| ASTMD256 | 360 J/m | ||
| ASTMD4812 | 2100 J/m | ||
| Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 95 kJ/m² |
| ISO180/1A | 25 kJ/m² | ||
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 26 kJ/m² |
| ISO180/1U | 130 kJ/m² |
| Electrical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/DX02437 |
|---|---|---|---|
| Surface Resistivity | ASTMD257 | 4.8E+07 ohms | |
| Volume Resistivity | ASTMD257 | 1.4E+07 ohms·cm |