PC D551RC-701 SABIC INNOVATIVE NANSHA
LNP™ THERMOCOMP™ Compound
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/D551RC-701
Melt Volume-Flow Rate (MVR)
300°C/5.0kg
ASTMD1238
cm3/10min
2
Melt mass flow rate
300°C/2.16kg
ASTMD1238
g/10min
1
Melt mass flow rate
300°C/5.0kg
ASTMD1238
g/10min
4
Shrinkage rate
MD:24小时
ASTMD955
%
0
Shrinkage rate
TD:24小时
ASTMD955
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/D551RC-701
--
ASTMD638
Mpa
1
--
ISO527-2/1
Mpa
1
Fracture
ASTMD638
Mpa
1
crack
ISO527-2/5
Mpa
1
Fracture
ASTMD638
%
2
crack
ISO527-2/5
%
1
Impact strength of simply supported beam gap
23°C
ISO179/1eA
kJ/m²
1
The impact strength of a simply supported beam without a notch is
23°C
ISO179/1eU
kJ/m²
3
Bending modulus
50.0mm跨距
ASTMD790
Mpa
1
bending strength
断裂,50.0mm跨距
ASTMD790
Mpa
2
Cantilever beam without notch impact strength
23°C
ASTMD4812
J/m
5
Dart impact equipped with measuring instruments
23°C,EnergyatPeakLoad
ASTMD3763
J
2
Thermal performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/D551RC-701
Hot deformation temperature
1.8MPa,未退火,3.20mm
ASTMD648
°C
1
Linear coefficient of thermal expansion
MD:-40到40°C
ASTME831
cm/cm/°C
1
Linear coefficient of thermal expansion
TD:-40到40°C
ASTME831
cm/cm/°C
5