Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC L-1225ZL100 TEIJIN SINGAPORE
PANLITE®
lens、Translucent accessories、Automotive sector、Application in the automo、Car headlights
UV resistance、transparent
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TEIJIN SINGAPORE/L-1225ZL100 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO179 | NoBreak | |
| Charpy Notched Impact Strength | ISO179 | 53 kJ/m² |
| Electrical performance | Test Condition | Test Method | TEIJIN SINGAPORE/L-1225ZL100 |
|---|---|---|---|
| Surface Resistivity | IEC60093 | >1.0E+15 ohms | |
| Dissipation Factor | 1MHz | IEC60250 | 9E-03 |
| Dielectric strength 3 | IEC60243-1 | 30 KV/mm | |
| CTI | IEC60112 | 250 V | |
| 1MHz | IEC60250 | 3.00 | |
| Volume resistivity | IEC60093 | >1.0E+15 ohms·cm | |
| 100Hz | IEC60250 | 3.10 | |
| Dissipation Factor | 100Hz | IEC60250 | 1E-03 |
| Mechanical properties | Test Condition | Test Method | TEIJIN SINGAPORE/L-1225ZL100 |
|---|---|---|---|
| Tensile stress | 屈服 | ISO527-2/50 | 62.0 Mpa |
| Tensile modulus | ISO527-2/1 | 2400 Mpa | |
| Bending modulus 2 | ISO178 | 2400 Mpa | |
| Bending stress 2 | ISO178 | 95.0 Mpa | |
| Tensile strain | 屈服 | ISO527-2/50 | 6.0 % |
| Nominal tensile fracture strain | ISO527-2/50 | >50 % |
| optical performance | Test Condition | Test Method | TEIJIN SINGAPORE/L-1225ZL100 |
|---|---|---|---|
| refractive index | ASTMD542 | 1.585 | |
| transmissivity | 3000µm | ASTMD1003 | 88.0 % |
| flammability | Test Condition | Test Method | TEIJIN SINGAPORE/L-1225ZL100 |
|---|---|---|---|
| Hot filament ignition temperature | 3.2mm | IEC60695-2-13 | 875 °C |
| Burning wire flammability index | 1.5mm | IEC60695-2-12 | 825 °C |
| UL flame retardant rating | 2.1mm | UL94 | HB |
| 0.40mm | UL94 | V-2 | |
| Burning wire flammability index | 3.2mm | IEC60695-2-12 | 875 °C |
| Hot filament ignition temperature | 1.5mm | IEC60695-2-13 | 850 °C |
| physical property | Test Condition | Test Method | TEIJIN SINGAPORE/L-1225ZL100 |
|---|---|---|---|
| Melt volume flow rate | 300°C/1.2kg | ISO1133 | 25.0 cm3/10min |
| Water absorption rate | 23°C,24hr | ISO62 | 0.20 % |
| density | ISO1183 | 1.20 g/cm³ | |
| Shrinkage rate | MD:4.00mm | 内部方法 | 0.50to0.70 % |
| TD:4.00mm | 内部方法 | 0.50to0.70 % |
| Thermal performance | Test Condition | Test Method | TEIJIN SINGAPORE/L-1225ZL100 |
|---|---|---|---|
| TD | ISO11359-2 | 7E-05 cm/cm/°C | |
| RTI Elec | 1.5mm | UL746 | 125 °C |
| 0.45MPa,未退火 | ISO75-2/B | 136 °C | |
| vicat | ISO306/B50 | 142 °C | |
| RTI Str | 1.5mm | UL746 | 125 °C |
| 1.8MPa,未退火 | ISO75-2/A | 123 °C | |
| RTI Imp | 1.5mm | UL746 | 115 °C |
| MD | ISO11359-2 | 7E-05 cm/cm/°C |