PA66 A3EG6 PA66 vs. - Plastic Material Properties Comparison Chart at Plas.com

Material Selector

All

Plastic Materials Additives Masterbatch Material Selector Price Index Trade Data Plastic News About Us

Material Comparison

Add Comparison Model

Select Products for Comparison (1/4)

Highlight Differences

Hide Same

Product Name / Manufacturer / Model

Grade

Certificates

Reference Price

PA66 BASF GERMANY A3EG6

Enhanced level

US$ 3,770 / MT

FOB Guangzhou port, China

thermal performance	Test Condition	Test Method	BASF GERMANY/A3EG6
Melting temperature		ISO 3146	260 °C
RTI Imp	3.0mm	UL 746	120 °C
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	1.5-2/6-7 mm/mm.℃
Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	250 °C
Melting temperature		ASTM D3418	260 °C
Linear coefficient of thermal expansion	TD		6.5E-05 cm/cm/°C
RTI Imp	1.5mm	UL 746	120 °C
RTI Elec	3.0mm	UL 746	120 °C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	250 °C
RTI Str	3.0mm	UL 746	130 °C
RTI Imp	6.0mm	UL 746	120 °C
Linear coefficient of thermal expansion	MD	ASTME831	1E-05 cm/cm/°C
Hot deformation temperature	HDT	ASTM D648/ISO 75	250 1.8Mpa ℃（℉）
RTI Str	1.5mm	UL 746	130 °C
RTI Str		6.0mm	UL 746	130 °C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	250 °C
Hot deformation temperature		1.8MPa,Unannealed	ASTM D648	250 °C
Linear coefficient of thermal expansion	MD		2.5E-05 cm/cm/°C
RTI Elec	1.5mm	UL 746	120 °C
RTI Elec		0.75mm	UL 746	120 °C
Combustibility (rate)		UL 94	94HB
Melting temperature			260 ℃（℉）
RTI Elec	6.0mm	UL 746	120 °C
other	Test Condition	Test Method	BASF GERMANY/A3EG6
characteristic			玻纤增强注射级.用于需要高刚性和尺寸稳定性的机械部件护罩.插座外罩.冷却风扇.汽车冷却系统水室以及电绝缘制品
Physical properties	Test Condition	Test Method	BASF GERMANY/A3EG6
Melt Volume Flow Rate (MVR)	275°C/5.0kg	ISO 1133	40.0 cm3/10min
melt mass-flow rate		ASTM D1238/ISO 1133	40 g/10min
Shrinkage rate	MD：3.18mm		0.30 %
density		ASTM D792/ISO 1183	1.36
Water absorption rate		ASTM D570/ISO 62	5.2-5.8 %
		Equilibrium,50%RH	ASTM D570	1.7 %
		Equilibrium,23°C,50%RH	ISO 62	1.7 %
		Saturation,23°C	ISO 62	5.5 %
		Saturation	ASTM D570	5.5 %
mechanical properties	Test Condition	Test Method	BASF GERMANY/A3EG6
bending strength	23°C	ISO 178	280 Mpa
Charpy Notched Impact Strength		ASTM D256/ISO 179	13/22 kg·cm/cm(J/M)ft·lb/in
tensile strength	Break,23°C	ASTM D638	186 Mpa
bending strength		ASTM D790/ISO 178	280/220 kg·cm/cm(J/M)ft·lb/in
Tensile strain	Break,-40°C	ISO 527-2	3.2 %
Bending modulus		ASTM D790/ISO 178	8600/7000 kg·cm/cm(J/M)ft·lb/in
Tensile modulus	23°C	ISO 527-2	10000 Mpa
Tensile strain	Break,23°C	ISO 527-2	3.0 %
tensile strength	Break,23°C	ISO 527-2	190 Mpa
Elongation at Break		ASTM D638/ISO 527	3/5 %
tensile strength	Break,-40°C	ISO 527-2	238 Mpa
Bending modulus	23°C	ISO 178	8600 Mpa
elongation	Break,23°C	ASTM D638	3.0 %
tensile strength		ASTM D638/ISO 527	10000/7200 kg/cm²(MPa)[Lb/in²]
Electrical performance	Test Condition	Test Method	BASF GERMANY/A3EG6
Dissipation factor	100Hz	IEC 60250	0.014
Volume resistivity	1.50mm	ASTM D257	1E+13 ohms·cm
Volume resistivity			IEC 60093	1E+13 ohms·cm
Dissipation factor	1MHz	IEC 60250	0.014
Dielectric constant	1MHz	IEC 60250	3.50
Surface resistivity		ASTM D257/IEC 60093	10^12/10^10 Ω
Compared to the anti leakage trace index		IEC 60112	PLC 1
Dielectric constant		ASTM D150/IEC 60250	3.6/5.6
Volume resistivity		ASTM D257/IEC 60093	10^15/10^12 Ω.cm
flammability	Test Condition	Test Method	BASF GERMANY/A3EG6
UL flame retardant rating	1.5mm	UL 94	HB
		6.0mm	UL 94	HB
		3.0mm	UL 94	HB
impact performance	Test Condition	Test Method	BASF GERMANY/A3EG6
Impact strength of simply supported beam without notch	-30°C	ISO 179	70 kJ/m²
Impact strength of simply supported beam without notch		23°C	ISO 179	85 kJ/m²