Impact resistance	Test Condition	Test Method	BASF GERMANY/A3EG6
Impact strength of simply supported beam without notch	-30°C	ISO 179	70 kJ/m²
Impact strength of simply supported beam without notch		23°C	ISO 179	85 kJ/m²

Electrical performance	Test Condition	Test Method	BASF GERMANY/A3EG6
Compared to the Leakage Tracking Index (CTI)		IEC 60112	PLC 1
Surface Resistivity		ASTM D257/IEC 60093	10^12/10^10 Ω
Volume resistivity		IEC 60093	1E+13 ohms·cm
dielectric constant		ASTM D150/IEC 60250	3.6/5.6
Volume resistivity	1.50mm	ASTM D257	1E+13 ohms·cm
Dissipation Factor	100Hz	IEC 60250	0.014
dielectric constant	1MHz	IEC 60250	3.50
Volume resistivity		ASTM D257/IEC 60093	10^15/10^12 Ω.cm
Dissipation Factor	1MHz	IEC 60250	0.014

Mechanical properties	Test Condition	Test Method	BASF GERMANY/A3EG6
tensile strength	断裂,-40°C	ISO 527-2	238 Mpa
Tensile modulus	23°C	ISO 527-2	10000 Mpa
Flexural modulus		ASTM D790/ISO 178	8600/7000 kg·cm/cm(J/M)ft·lb/in
bending strength		ASTM D790/ISO 178	280/220 kg·cm/cm(J/M)ft·lb/in
tensile strength	断裂,23°C	ISO 527-2	190 Mpa
elongation at break		ASTM D638/ISO 527	3/5 %
Tensile strain	断裂,-40°C	ISO 527-2	3.2 %
tensile strength	断裂,23°C	ASTM D638	186 Mpa
tensile strength			ASTM D638/ISO 527	10000/7200 kg/cm²(MPa)[Lb/in²]
Tensile strain	断裂,23°C	ISO 527-2	3.0 %
bending strength	23°C	ISO 178	280 Mpa
Flexural modulus	23°C	ISO 178	8600 Mpa
Charpy Notched Impact Strength		ASTM D256/ISO 179	11 kg·cm/cm(J/M)ft·lb/in
elongation	断裂,23°C	ASTM D638	3.0 %

other	Test Condition	Test Method	BASF GERMANY/A3EG6
characteristic			玻纤增强注射级.用于需要高刚性和尺寸稳定性的机械部件护罩.插座外罩.冷却风扇.汽车冷却系统水室以及电绝缘制品

Physical properties	Test Method	BASF GERMANY/A3EG6
density	ASTM D792/ISO 1183	1.36
melt mass-flow rate	ASTM D1238/ISO 1133	40 g/10min
Water absorption rate	ASTM D570/ISO 62	5.2-5.8 %

flammability	Test Condition	Test Method	BASF GERMANY/A3EG6
UL flame retardant rating	3.0mm	UL 94	HB
		6.0mm	UL 94	HB
		1.5mm	UL 94	HB

physical property	Test Condition	Test Method	BASF GERMANY/A3EG6
Shrinkage rate	MD：3.18mm		0.30 %
Water absorption rate	饱和	ASTM D570	5.5 %
		平衡,50%RH	ASTM D570	1.7 %
		平衡,23°C,50%RH	ISO 62	1.7 %
		饱和,23°C	ISO 62	5.5 %
Melt volume flow rate	275°C/5.0kg	ISO 1133	40.0 cm3/10min

Thermal performance	Test Condition	Test Method	BASF GERMANY/A3EG6
Combustibility (rate)		UL 94	94HB
RTI Elec	6.0mm	UL 746	120 °C
Heat distortion temperature	1.8MPa,未退火，HDT	ASTM D648	250 °C
RTI Imp	1.5mm	UL 746	120 °C
RTI Str	6.0mm	UL 746	130 °C
melting temperature		ASTM D3418	260 °C
RTI Elec	3.0mm	UL 746	120 °C
RTI Imp	3.0mm	UL 746	120 °C
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	1.5-2/6-7 mm/mm.℃
melting temperature		ISO 3146	260 °C
RTI Elec	0.75mm	UL 746	120 °C
Heat distortion temperature	0.45MPa,未退火，HDT	ASTM D648	250 °C
		HDT	ASTM D648/ISO 75	250 1.8Mpa ℃（℉）
		0.45MPa,未退火，HDT	ISO 75-2/B	250 °C
Linear coefficient of thermal expansion	MD		2.5E-05 cm/cm/°C
RTI Str	1.5mm	UL 746	130 °C
Heat distortion temperature	1.8MPa,未退火，HDT	ISO 75-2/A	250 °C
RTI Str	3.0mm	UL 746	130 °C
RTI Elec	1.5mm	UL 746	120 °C
melting temperature			260 ℃（℉）
Linear coefficient of thermal expansion	MD	ASTME831	1E-05 cm/cm/°C
RTI Imp	6.0mm	UL 746	120 °C
Linear coefficient of thermal expansion	TD		6.5E-05 cm/cm/°C