Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC DFL-4034 BK SABIC INNOVATIVE US
LNP™ LUBRICOMP™
Casters、Electronic and Electrical
Easy to demould、Easy to form
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/DFL-4034 BK |
|---|---|---|---|
| 1.8MPa, Unannealed,64.0mm Span | ISO75-2/Af | 141 °C | |
| 0.45MPa, Unannealed,3.20mm Span | ISO75-2/Bf | 146 °C | |
| 1.8MPa, Unannealed,3.20mm | ASTMD648 | 142 °C | |
| Linear thermal expansion coefficient | MD:-30到30°C | ASTMD696 | 3.7E-05 cm/cm/°C |
| 0.45MPa, Unannealed,3.20mm | ASTMD648 | 146 °C | |
| Linear thermal expansion coefficient | TD:-30到30°C | ASTMD696 | 6.3E-05 cm/cm/°C |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/DFL-4034 BK |
|---|---|---|---|
| Equilibrium,23°C,50%RH | ISO62 | 0.13 % | |
| Modeling Shrinkage | TD:24小时 | ASTMD955 | 0.20到0.40 % |
| ASTMD570 | 0.090 % | ||
| Modeling Shrinkage | MD:24小时 | ASTMD955 | 0.020到0.040 % |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/DFL-4034 BK |
|---|---|---|---|
| Break | ASTMD638 | 95.0 Mpa | |
| yield | ISO527-2/5 | 2.8 % | |
| fracture | ISO527-2/5 | 3.1 % | |
| ISO178 | 6200 Mpa | ||
| Break,50.0mm Span | ASTMD790 | 145 Mpa | |
| ASTMD638 | 7190 Mpa | ||
| fracture | ISO527-2/5 | 93.0 Mpa | |
| Break | ASTMD638 | 2.7 % | |
| Specific Wear Rate | Ring | ASTMD3702Modified | 13.0 10^-10in^5-min/ft-lb-hr |
| Coefficient of Friction | 与自身-静态 | ASTMD3702Modified | 0.50 |
| 50.0mm Span | ASTMD790 | 6320 Mpa | |
| Specific Wear Rate | Washer | ASTMD3702Modified | 89.0 10^-10in^5-min/ft-lb-hr |
| Coefficient of Friction | 与自身-动态 | ASTMD3702Modified | 0.46 |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/DFL-4034 BK |
|---|---|---|---|
| ASTMD3763 | 19.6 J | ||
| ASTMD256 | 150 J/m | ||
| ASTMD4812 | 740 J/m | ||
| ISO180/1A | 14 kJ/m² | ||
| ISO180/1U | 49 kJ/m² |