TPU A 60 E 4902 HUNTSMAN SHANGHAI
AVALON®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | HUNTSMAN SHANGHAI/A 60 E 4902 |
|---|---|---|---|
| Shore hardness | 邵氏A,注塑 | DIN 53505 | 55 |
| 邵氏A,注塑 | ASTM D2240 | 56 | |
| 邵氏D,注塑 | ASTM D2240 | 15 | |
| 邵氏D,注塑 | DIN 53505 | 15 |
| Mechanical properties | Test Condition | Test Method | HUNTSMAN SHANGHAI/A 60 E 4902 |
|---|---|---|---|
| wear resistance | -- | DIN 53516 | 43 mm³ |
| -- | ASTM D395 | 43 mm³ |
| physical property | Test Condition | Test Method | HUNTSMAN SHANGHAI/A 60 E 4902 |
|---|---|---|---|
| Melt volume flow rate | 160°C/8.7kg | 35.0 cm3/10min |
| elastomer | Test Condition | Test Method | HUNTSMAN SHANGHAI/A 60 E 4902 |
|---|---|---|---|
| tear strength | 0.635mm | ASTM D624 | 35.9 kN/m |
| compression set | 23°C,70hr | ASTM D395 | 40 % |
| Tensile strain | Break,0.635mm | DIN 53504 | 900 % |
| compression set | 70°C,24hr | ASTM D395 | 80 % |
| Shore hardness | ASTM D2632 | 60 % | |
| tensile strength | Break,0.635mm | ASTM D412 | 7.52 Mpa |
| compression set | 200%Strain | DIN 53504 | 8 % |
| tensile strength | Break,0.635mm | DIN 53504 | 10.0 Mpa |
| Tensile strain | Break,0.635mm | ASTM D412 | 720 % |
| compression set | 70°C,24hr | DIN 53517 | 60 % |
| 23°C,70hr | DIN 53517 | 35 % | |
| tensile strength | 100%Strain,0.635mm | DIN 53504 | 1.40 Mpa |
| compression set | 200%Strain | ASTM D412 | 8 % |
| tear strength | 0.635mm | DIN 53515 | 25 kN/m |
| tensile strength | 300%Strain,0.635mm | ASTM D412 | 4.07 Mpa |
| 300%Strain,0.635mm | DIN 53504 | 2.40 Mpa | |
| 100%Strain,0.635mm | ASTM D412 | 2.34 Mpa |
| Thermal performance | Test Condition | Test Method | HUNTSMAN SHANGHAI/A 60 E 4902 |
|---|---|---|---|
| melting temperature | 内部方法 | 98.9to130 °C | |
| TMA | High:635.0µm | 内部方法 | 145 °C |
| Low:635.0µm | 内部方法 | 110 °C |