PC S-1000UR MITSUBISHI THAILAND
IUPILON™
Electrical applications、Automotive Applications
high viscosity、UV resistance、high viscosity
TDS
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Electrical performance | Test Condition | Test Method | MITSUBISHI THAILAND/S-1000UR |
|---|---|---|---|
| Volume resistivity | IEC 93 | 3E+14 Ω.m | |
| dielectric constant | 1MHz | IEC 250 | 3.1 |
| Dielectric loss | 1MHz | IEC 250 | 0.0090 |
| 100HZ | IEC 250 | 0.0006 | |
| dielectric constant | 100HZ | IEC 250 | 3.1 |
| dielectric strength | 1mm | IEC 243-1 | 31 MV/m |
| Volume resistivity | IEC 93 | 6E+15 Ω | |
| dielectric strength | 3mm | IEC 243-1 | 18 MV/m |
| Compared to the Leakage Traceability Index (CTI) | IEC 112 | 275 |
| Mechanical properties | Test Condition | Test Method | MITSUBISHI THAILAND/S-1000UR |
|---|---|---|---|
| Impact strength of cantilever beam gap | ISO 179 | 84 KJ/m | |
| Tensile stress | 屈服 | ISO 527-2 | 60 Mpa |
| bending strength | ISO 178 | 93 Mpa | |
| Flexural modulus | ISO 178 | 2300 Mpa | |
| Tensile strain | 屈服 | 5.5 % | |
| Tensile modulus | ISO 527-1 | 2400 Mpa | |
| elongation | 断裂 | 105 % |
| physical property | Test Condition | Test Method | MITSUBISHI THAILAND/S-1000UR |
|---|---|---|---|
| Shrinkage rate | 平行方向 | 0.5-0.7 % | |
| 垂直方向 | 0.5-0.7 % | ||
| melt mass-flow rate | ISO 1133 | 7.5 g/10min | |
| Water absorption rate | 23℃,24hrs | 0.24 % |
| Thermal performance | Test Condition | Test Method | MITSUBISHI THAILAND/S-1000UR |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa，HDT | ISO 75-2 | 145 °C |
| Linear coefficient of thermal expansion | MD | 6.5E-05 1/℃ | |
| Heat distortion temperature | 1.80MPa，HDT | ISO 75-1 | 131 °C |
| Linear coefficient of thermal expansion | TD | 6.6E-05 1/℃ |