Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPO(PPE)+PS+PA NORYL GTX™ GTX989 resin SABIC
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC/NORYL GTX™ GTX989 resin |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 22 kJ/m² |
| Impact strength of cantilever beam gap | -30°C8 | ISO 180/1A | 15 kJ/m² |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 60.0 J |
| Impact strength of cantilever beam gap | -30°C | ASTM D256 | 180 J/m |
| 23°C | ASTM D256 | 240 J/m | |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 15 kJ/m² |
| Impact strength of cantilever beam gap | 23°C8 | ISO 180/1A | 22 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC/NORYL GTX™ GTX989 resin |
|---|---|---|---|
| tensile strength | 屈服3 | ASTM D638 | 65.0 MPa |
| elongation | 断裂3 | ASTM D638 | 45 % |
| 断裂 | ISO 527-2/50 | 40 % | |
| Flexural modulus | --5 | ISO 178 | 2300 MPa |
| Tensile modulus | -- | ISO 527-2/1 | 2300 MPa |
| bending strength | 屈服,50.0mm跨距4 | ASTM D790 | 95.0 MPa |
| tensile strength | 屈服 | ISO 527-2/50 | 60.0 MPa |
| Flexural modulus | 50.0mm跨距4 | ASTM D790 | 2450 MPa |
| bending strength | --5,6 | ISO 178 | 90.0 MPa |
| elongation | 屈服 | ISO 527-2/50 | 5.0 % |
| 屈服3 | ASTM D638 | 5.0 % | |
| tensile strength | 断裂3 | ASTM D638 | 60.0 MPa |
| 断裂 | ISO 527-2/50 | 55.0 MPa | |
| Tensile modulus | --2 | ASTM D638 | 2350 MPa |
| Electrical performance | Test Condition | Test Method | SABIC/NORYL GTX™ GTX989 resin |
|---|---|---|---|
| Volume resistivity | 内部方法 | 1.0E+3到1.0E+4 ohms·cm |
| physical property | Test Condition | Test Method | SABIC/NORYL GTX™ GTX989 resin |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 1.2to1.6 % |
| Melt volume flow rate | 280°C/5.0kg | ISO 1133 | 19.0 cm³/10min |
| density | ASTMD792 | 1.08 g/cm³ | |
| melt mass-flow rate | 280°C/5.0kg | ASTM D1238 | 16 g/10min |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 1.2 % |
| 饱和,23°C | ISO 62 | 4.2 % |
| Thermal performance | Test Condition | Test Method | SABIC/NORYL GTX™ GTX989 resin |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD:-40到60°C | ASTME831 | 8.5E-05 cm/cm/°C |
| vicat | -- | ISO 306/B120 | 200 °C |
| Linear coefficient of thermal expansion | TD:23到60°C | ISO 11359-2 | 9E-05 cm/cm/°C |
| MD:23到60°C | ISO 11359-2 | 9E-05 cm/cm/°C | |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 190 °C |
| 0.45MPa,未退火,100mm跨距9，HDT | ISO 75-2/Be | 190 °C | |
| vicat | -- | ASTMD152510 | 195 °C |
| Linear coefficient of thermal expansion | MD:-40到60°C | ASTME831 | 8.5E-05 cm/cm/°C |