PPS OX11315 BK SABIC INNOVATIVE US
LNP™ KONDUIT™
Automotive Applications
Carbon fiber reinforced,High impact resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/OX11315 BK |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 3.9 kJ/m² |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 5.14 J |
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 1.14 J | |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 1.7 kJ/m² |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/OX11315 BK |
|---|---|---|---|
| Surface Resistivity | ASTM D257 | 2.4E+15 ohms |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/OX11315 BK |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 18400 Mpa | |
| ASTM D638 | 30100 Mpa | ||
| tensile strength | 断裂 | ISO 527-2/5 | 54.0 Mpa |
| elongation | 断裂 | ASTM D638 | 0.20 % |
| bending strength | ISO 178 | 84.0 Mpa | |
| Flexural modulus | ISO 178 | 21400 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/5 | 0.30 % |
| tensile strength | 断裂 | ASTM D638 | 41.0 Mpa |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 26500 Mpa |
| bending strength | 断裂,50.0mm跨距 | ASTM D790 | 82.0 Mpa |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/OX11315 BK |
|---|---|---|---|
| UL flame retardant rating | 2.5mm | UL 94 | 5VA |
| 1.0mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/OX11315 BK |
|---|---|---|---|
| Shrinkage rate | MD：24小时 | ASTM D955 | 0.34 % |
| Water absorption rate | 24hr,50%RH | ASTM D570 | 0.010 % |
| 平衡,23°C,50%RH | ISO 62 | <0.010 % | |
| Shrinkage rate | TD：24hr | ASTM D955 | 0.44 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/OX11315 BK |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Bf | 275 °C |
| thermal conductivity | --9 | ASTM D790/ISO 178 | 15 W/m/K |
| --8 | ASTM D790/ISO 178 | 3.5 W/m/K | |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 275 °C |
| RTI Imp | UL 746 | 130 °C | |
| Heat distortion temperature | 1.8MPa,未退火,64.0mm跨距，HDT | ISO 75-2/Af | 238 °C |
| RTI Str | UL 746 | 130 °C | |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 242 °C |
| specific heat | ASTMC351 | 1260 J/kg/°C | |
| RTI Elec | UL 746 | 130 °C |