Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PUR-Capro C900 CHEMTURU USA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Supplementary Information | Test Condition | Test Method | CHEMTURU USA/ C900 |
|---|---|---|---|
| Wear factor | DIN2 | 592 | |
| DIN3 | 890 | ||
| NBS2 | 1300 % | ||
| NBS3 | 1700 % |
| hardness | Test Condition | Test Method | CHEMTURU USA/ C900 |
|---|---|---|---|
| Shore hardness | 邵氏A3 | ASTM D2240 | 87to89 |
| 邵氏A2 | ASTM D2240 | 86to89 |
| film | Test Condition | Test Method | CHEMTURU USA/ C900 |
|---|---|---|---|
| Tear resistance of pants | --3 | ASTM D1938 | 42.7 N/mm |
| --2 | ASTM D1938 | 33.3 N/mm |
| Mechanical properties | Test Condition | Test Method | CHEMTURU USA/ C900 |
|---|---|---|---|
| Wear factor | --2，相对体积损失 | 25.0 mm³ | |
| --3，相对体积损失 | 17.0 mm³ |
| thermosetting | Test Condition | Test Method | CHEMTURU USA/ C900 |
|---|---|---|---|
| stripping time | 140°C | 10 min | |
| Post curing time | 120°C5 | 16to24 hr | |
| stripping time | 120°C | 20 min | |
| STORAGE STABILITY | 70°C | 120 min | |
| 50°C | 1400 min | ||
| Post curing time | 140°C6 | 16to24 hr |
| elastomer | Test Condition | Test Method | CHEMTURU USA/ C900 |
|---|---|---|---|
| Shore hardness | --2 | ASTM D2632 | 52 % |
| Falling ball impact strength | --2 | 64 % | |
| Shore hardness | --3 | ASTM D2632 | 52 % |
| Falling ball impact strength | --3 | 64 % | |
| tear strength | --4,3 | ASTM D624 | 83.0 kN/m |
| compression set | 100°C,22hr3 | ASTM D395B | 47 % |
| tear strength | --4,2 | ASTM D624 | 70.1 kN/m |
| tensile strength | 300%应变2 | ASTM D412 | 8.06 MPa |
| compression set | 70°C,22hr2 | ASTM D395B | 31 % |
| tensile strength | --2 | ASTM D412 | 39.2 MPa |
| --3 | ASTM D412 | 42.2 MPa | |
| tear strength | 开裂2 | ASTM D470 | 19 kN/m |
| 开裂3 | ASTM D470 | 20 kN/m | |
| compression set | 70°C,22hr3 | ASTM D395B | 27 % |
| tensile strength | 100%应变2 | ASTM D412 | 6.17 MPa |
| 100%应变3 | ASTM D412 | 6.29 MPa | |
| 300%应变3 | ASTM D412 | 8.54 MPa | |
| compression set | 100°C,22hr2 | ASTM D395B | 54 % |
| elongation | 断裂3 | ASTM D412 | 570 % |
| 断裂2 | ASTM D412 | 540 % |
| physical property | Test Condition | Test Method | CHEMTURU USA/ C900 |
|---|---|---|---|
| density | ASTM D792 | 1.13 g/cm³ |