ABS Nilac F17 V0 Soredi S.p.a.
--
--
Filler, glass fiber reinforced material, 17%, filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Soredi S.p.a./Nilac F17 V0 |
|---|---|---|---|
| Impact strength of cantilever beam gap | -20°C,3.20mm | ASTM D256 | 40 J/m |
| 23°C,3.20mm | ASTM D256 | 60 J/m |
| hardness | Test Condition | Test Method | Soredi S.p.a./Nilac F17 V0 |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 110 |
| Mechanical properties | Test Condition | Test Method | Soredi S.p.a./Nilac F17 V0 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 2.0 % |
| bending strength | 断裂 | ASTM D790 | 70.0 MPa |
| tensile strength | 断裂 | ASTM D638 | 65.0 MPa |
| Flexural modulus | ASTM D790 | 6000 MPa |
| flammability | Test Condition | Test Method | Soredi S.p.a./Nilac F17 V0 |
|---|---|---|---|
| Hot filament ignition temperature | IEC 60695-2-13 | 960 °C | |
| UL flame retardant rating | 3.2mm | UL 94 | V-0 |
| 1.6mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | Soredi S.p.a./Nilac F17 V0 |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D955 | 0.20to0.40 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.20 % |
| density | ASTM D792 | 1.35 g/cm³ | |
| melt mass-flow rate | 220°C/10.0kg | ASTM D1238 | 8.0 g/10min |
| Thermal performance | Test Condition | Test Method | Soredi S.p.a./Nilac F17 V0 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 100 °C |
| vicat | ASTM D15254 | 105 °C | |
| Linear coefficient of thermal expansion | MD：23到55°C | ISO 11359-2 | 4E-05 cm/cm/°C |