PS CA3896 Cabot Corporation
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Cabot Corporation/ CA3896 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ISO 180 | 16 kJ/m² |
| hardness | Test Condition | Test Method | Cabot Corporation/ CA3896 |
|---|---|---|---|
| Shore hardness | 邵氏D,15秒 | ASTM D2240 | 75 |
| Mechanical properties | Test Condition | Test Method | Cabot Corporation/ CA3896 |
|---|---|---|---|
| Tensile strain | 断裂 | ISO 527-2 | 23 % |
| tensile strength | 断裂 | ISO 527-2 | 24.3 MPa |
| 屈服 | ISO 527-2 | 30.4 MPa | |
| Flexural modulus | ISO 178 | 1880 MPa |
| Electrical performance | Test Condition | Test Method | Cabot Corporation/ CA3896 |
|---|---|---|---|
| Volume resistivity | 0.400mm | 内部方法 | 2.1E+03 ohms |
| 内部方法 | 3E+02 ohms·cm |
| flammability | Test Condition | Test Method | Cabot Corporation/ CA3896 |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | UL 94 | HB |
| physical property | Test Condition | Test Method | Cabot Corporation/ CA3896 |
|---|---|---|---|
| melt mass-flow rate | 200°C/21.6kg | ISO 1133 | 38 g/10min |
| 200°C/10.0kg | ISO 1133 | 5.0 g/10min | |
| 200°C/5.0kg | ISO 1133 | 1.0 g/10min | |
| density | 23°C | 内部方法 | 1.09 g/cm³ |
| Thermal performance | Test Condition | Test Method | Cabot Corporation/ CA3896 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 72.0 °C |
| vicat | ISO 306/A | 101 °C |