Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 BKV15H1.0 ENVALIOR WUXI
Durethan®
Home appliance components、Automotive Applications、Electronic and electrical
Glass fiber reinforced
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | ENVALIOR WUXI/BKV15H1.0 |
|---|---|---|---|
| -30°C | ISO180/1U | 20 kJ/m² | |
| 23°C | ISO180/1U | 25 kJ/m² | |
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | 40 kJ/m² |
| -30°C | ISO179/1eU | 35 kJ/m² |
| hardness | Test Condition | Test Method | ENVALIOR WUXI/BKV15H1.0 |
|---|---|---|---|
| ISO2039-1 | 190 Mpa |
| Supplementary Information | Test Condition | Test Method | ENVALIOR WUXI/BKV15H1.0 |
|---|---|---|---|
| ISO Shortcut | ISO1874 | PA6/66,GHR,14-060,GF15 |
| film | Test Condition | Test Method | ENVALIOR WUXI/BKV15H1.0 |
|---|---|---|---|
| --6 | ISO6603-2 | 505 N | |
| --7 | ISO6603-2 | 2.00 J | |
| --6 | ISO6603-2 | 1.50 J | |
| --7 | ISO6603-2 | 560 N |
| Electrical performance | Test Condition | Test Method | ENVALIOR WUXI/BKV15H1.0 |
|---|---|---|---|
| Surface Resistivity | IEC60093 | 1E+15 ohms | |
| Volume resistivity | 23°C | IEC60093 | 1E+13 ohms·cm |
| 23°C,100Hz | IEC60250 | 4.10 | |
| 23°C,1MHz | IEC60250 | 3.70 | |
| CTI | 解决方案A | IEC60112 | 375 V |
| dielectric strength | 23°C,1.00mm | IEC60243-1 | 30 KV/mm |
| Dissipation Factor | 23°C,100Hz | IEC60250 | 8E-03 |
| 23°C,1MHz | IEC60250 | 0.018 |
| Mechanical properties | Test Condition | Test Method | ENVALIOR WUXI/BKV15H1.0 |
|---|---|---|---|
| Flexural modulus | 23°C | ISO178/A | 5700 Mpa |
| 23°C | ASTMD790 | 5700 Mpa | |
| Bending stress | 23°C | ISO178 | 185 Mpa |
| Tensile modulus | 23°C | ASTMD638 | 6310 Mpa |
| Bending stress | 3.5%Strain | ISO178/A | -- Mpa |
| Tensile strain | 断裂,23°C | ISO527-2/5 | 3.0 % |
| elongation | 断裂,23°C | ASTMD638 | 3.0 % |
| Tensile stress | 断裂,23°C | ISO527-2/5 | 120 Mpa |
| tensile strength | 断裂,23°C | ASTMD638 | 117 Mpa |
| Tensile modulus | 23°C | ISO527-2/1 | 6300 Mpa |
| bending strength | 23°C | ASTMD790 | 185 Mpa |
| Bending stress | FlexuralStrainatFlexuralStrength5(23°C) | 4.0 % |
| flammability | Test Condition | Test Method | ENVALIOR WUXI/BKV15H1.0 |
|---|---|---|---|
| Burning wire flammability index | 2.0mm | IEC60695-2-12 | 650 °C |
| Extreme Oxygen Index 9 | ISO4589-2 | 23 % | |
| UL flame retardant rating | 3.2mm | UL94 | HB |
| 1.6mm | UL94 | HB | |
| BurningBehavior10 | ISO3795 | passed |
| physical property | Test Condition | Test Method | ENVALIOR WUXI/BKV15H1.0 |
|---|---|---|---|
| Water absorption rate | 平衡,23°C,50%RH | ISO62 | 2.6 % |
| 饱和,23°C | ISO62 | 7.8 % | |
| Shrinkage rate | MD:120°C,2hr,3.00mm3 | ISO2577 | 0.10 % |
| TD:280°C,3.00mm2 | ISO2577 | 0.67 % | |
| Apparent density | ISO60 | 0.70 g/cm³ | |
| Shrinkage rate | MD:280°C,3.00mm2 | ISO2577 | 0.34 % |
| TD:120°C,2hr,3.00mm3 | ISO294-4 | 0.21 % |
| Thermal performance | Test Condition | Test Method | ENVALIOR WUXI/BKV15H1.0 |
|---|---|---|---|
| 0.45MPa,未退火 | ISO75-2/B | 210 °C | |
| 1.8MPa,未退火 | ISO75-2/A | 180 °C | |
| 8.0MPa,未退火 | ISO75-2/C | 55.0 °C | |
| vicat | -- | ISO306/B50 | 200 °C |
| -- | ISO306/B120 | 200 °C | |
| Melting temperature 5 | ISO11357-3 | 218 °C | |
| TD：23to55°C | ISO11359-2 | 8E-05 cm/cm/°C | |
| MD：23到55°C | ISO11359-2 | 3E-05 cm/cm/°C |