PC/PET X7300CL SABIC INNOVATIVE US
XYLEX™
Automotive sector
UV resistance、High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/X7300CL |
|---|---|---|---|
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 95.0 J |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 9.0 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/X7300CL |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 1900 Mpa | |
| elongation | 屈服 | ASTM D638 | 5.0 % |
| tensile strength | 断裂 | ASTM D638 | 52.0 Mpa |
| Tensile strain | 屈服 | ISO 527-2/50 | 5.0 % |
| tensile strength | 断裂 | ISO 527-2/50 | 55.0 Mpa |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 1940 Mpa |
| Tensile modulus | ASTM D638 | 1840 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 55.0 Mpa |
| elongation | 断裂 | ASTM D638 | 150 % |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 83.0 Mpa |
| ISO 178 | 71.0 Mpa | ||
| Flexural modulus | ISO 178 | 2000 Mpa | |
| tensile strength | 屈服 | ASTM D638 | 49.0 Mpa |
| Tensile strain | 断裂 | ISO 527-2/50 | >150 % |
| optical performance | Test Condition | Test Method | SABIC INNOVATIVE US/X7300CL |
|---|---|---|---|
| Haze ratio | 2540µm | ASTM D1003 | 2.0 % |
| transmissivity | 2540µm | ASTM D1003 | 88.0 % |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/X7300CL |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.40-0.80 % |
| melt mass-flow rate | 265°C/2.16kg | ASTM D1238 | 21 g/10min |
| Shrinkage rate | TD：3.20mm | 内部方法 | 0.50-0.70 % |
| Melt volume flow rate | 265°C/2.16kg | ISO 1133 | 21.0 cm3/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/X7300CL |
|---|---|---|---|
| Linear coefficient of thermal expansion | MD：23到60°C | ISO 11359-2 | 8.5E-05 cm/cm/°C |
| TD：-40到40°C | ASTME831 | 1.1E-04 cm/cm/°C | |
| vicat | ISO 306/B120 | 106 °C | |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 102 °C |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 1.2E-04 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,Unannealed,100mmSpan，HDT | ISO 75-2/Ae | 90.0 °C |
| Linear coefficient of thermal expansion | TD：23to60°C | ISO 11359-2 | 8.5E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 88.0 °C |
| vicat | ASTM D15259 | 108 °C |