| Impact resistance | Test Condition | Test Method | DUPONT USA/103HSL |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 5.5 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 400kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 4.5 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | NoBreak |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 6.0 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | NoBreak |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 5.0 kJ/m² |
| -40°C | ISO 180/1A | 5.5 kJ/m² | |
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 300kJ/m² |
| Supplementary Information | Test Condition | Test Method | DUPONT USA/103HSL |
|---|---|---|---|
| Odor | VDA270 | 2.50 | |
| Emissions of Organic Compounds | VDA277 | 2.10 µgC/g |
| film | Test Condition | Test Method | DUPONT USA/103HSL |
|---|---|---|---|
| Tensile strain | Yield，MD | ISO 527-3 | 4.5 % |
| thermal performance | Test Condition | Test Method | DUPONT USA/103HSL |
|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 70.0 °C |
| 0.45MPa,未退火，HDT | ISO 75-2/B | 200 °C | |
| vicat | ISO 306/B50 | 240 °C | |
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 1.1E-04 cm/cm/°C |
| Effective thermal diffusivity coefficient | 5E-08 m²/s | ||
| melting temperature | ISO 11357-3 | 262 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1E-04 cm/cm/°C |
| Glass Transition Temperature | ISO 11357-2 | 60.0 °C |
| mechanical properties | Test Condition | Test Method | DUPONT USA/103HSL |
|---|---|---|---|
| Nominal tensile fracture strain | ISO 527-2 | 20 % | |
| Tensile creep modulus | 1hr | ISO 899-1 | -- Mpa |
| Tensile modulus | ISO 527-2 | 3100 Mpa | |
| tensile strength | 屈服 | ISO 527-2 | 85.0 Mpa |
| Tensile strain | 屈服 | ISO 527-2 | 4.5 % |
| Tensile creep modulus | 1000hr | ISO 899-1 | -- Mpa |
| flexural modulus | ISO 178 | 2800 Mpa |
| Electrical performance | Test Condition | Test Method | DUPONT USA/103HSL |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 0 | |
| dielectric strength | IEC 60243-1 | 31 KV/mm | |
| relative permittivity | 100Hz | IEC 60250 | 3.80 |
| Dissipation Factor | 100Hz | IEC 60250 | 7.5E-03 |
| Compared to the Leakage Tracking Index (CTI) | 3.00mm | UL 746 | PLC 0 |
| volume resistivity | IEC 60093 | 1E+15 ohms·cm | |
| relative permittivity | 1MHz | IEC 60250 | 3.50 |
| Dissipation Factor | 1MHz | IEC 60250 | 0.017 |
| Physical properties | Test Condition | Test Method | DUPONT USA/103HSL |
|---|---|---|---|
| Water absorption rate | 平衡,23°C,2.00mm,50%RH | ISO 62 | 2.6 % |
| viscosity number | ISO 307 | 145 cm³/g | |
| ThermalConductivityofMelt | 0.16 W/m/K | ||
| SpecificHeatCapacity of Melt | 2790 J/kg/°C | ||
| density | ISO 1183 | 1.14 g/cm³ | |
| shrinkage rate | TD | ISO 294-4 | 1.3 % |
| MediumDensity | 0.980 g/cm³ | ||
| Ejection Temperature | 190 °C | ||
| Water absorption rate | 饱和,23°C,2.00mm | ISO 62 | 8.5 % |
| shrinkage rate | MD | ISO 294-4 | 1.3 % |
| flammability | Test Condition | Test Method | DUPONT USA/103HSL |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | IEC 60695-11-10,-20 | V-2 |
| FMVSS flammability | FMVSS302 | SE | |
| UL flame retardant rating | 0.71mm | IEC 60695-11-10,-20 | V-2 |
| 1.5mm | UL 94 | V-2 | |
| Limiting Oxygen Index | ISO 4589-2 | 28 % | |
| UL flame retardant rating | 0.71mm | UL 94 | V-2 |