PPO 100V ASAHI JAPAN
XYRON™
Industrial machinery、Automotive Applications
Aging resistance、Chemical resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Basic performance | Test Condition | Test Method | ASAHI JAPAN/100V |
|---|---|---|---|
| Shrinkage rate | ASTM D-955 | 0.50-0.70 % | |
| Water absorption rate | ASTM D-570 | 0.10 % | |
| density | ASTM D-792 | 1.08 g/cm |
| Mechanical properties | Test Condition | Test Method | ASAHI JAPAN/100V |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 56 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 2160 kg/cm²(MPa)[Lb/in²] | |
| ASTM D-790 | 2300 Mpa | ||
| bending strength | ASTM D-790 | 56 Mpa | |
| UL flame retardant rating | UL 94 | V-1 | |
| elongation at break | ASTM D638/ISO 527 | 40 % | |
| tensile strength | ASTM D-638 | 37.0 Mpa | |
| Rockwell hardness | ASTM D785 | R109 | |
| tensile strength | ASTM D638/ISO 527 | 34 kg/cm²(MPa)[Lb/in²] | |
| elongation at break | ASTM D-638 | 40 % |
| Physical properties | Test Condition | Test Method | ASAHI JAPAN/100V |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.08 | |
| Water absorption rate | ASTM D570/ISO 62 | 0.1 % |
| processability | Test Condition | Test Method | ASAHI JAPAN/100V |
|---|---|---|---|
| Temperature | 40-70 °C |
| Thermal performance | Test Condition | Test Method | ASAHI JAPAN/100V |
|---|---|---|---|
| Combustibility (rate) | UL 94 | v-1 | |
| Heat distortion temperature | HDT | ASTM D648/ISO 75 | 85 ℃（℉） |