Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/ABS CX7240-701 SABIC INNOVATIVE NANSHA
CYCOLOY™
Electrical field、Electronic field、Architectural application、Outdoor applications、Engine hood parts、Medical supplies、Nursing supplies、Plastic bag、Casters、Aerospace Applications、Liquid handling
Flame retardant、High impact resistance、High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/ABS/SABIC INNOVATIVE NANSHA/CX7240-701
density
ASTMD792
g/cm³
1
density
ISO1183
g/cm³
1
Melt Volume-Flow Rate (MVR)
260°C/2.16kg
ISO1133
cm3/10min
1
Melt mass flow rate
260°C/2.16kg
ASTMD1238
g/10min
1
Shrinkage rate
MD：3.20mm
内部方法
%
0
Water absorption rate
饱和,23°C
ISO62
%
0
Water absorption rate
平衡,23°C,50%RH
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/ABS/SABIC INNOVATIVE NANSHA/CX7240-701
Charpy Notched Impact Strength
-30°C7
ISO179/1eA
kJ/m²
1
Charpy Notched Impact Strength
23°C8
ISO179/1eA
kJ/m²
2
Charpy Notched Impact Strength
23°C7
ISO179/1eA
kJ/m²
2
Tensile modulus
ASTMD638
Mpa
2
Tensile modulus
ISO527-2/1
Mpa
2
tensile strength
屈服
ASTMD638
Mpa
6
tensile strength
屈服
ISO527-2/50
Mpa
6
tensile strength
断裂
ASTMD638
Mpa
5
tensile strength
断裂
ISO527-2/50
Mpa
5
elongation
屈服
ASTMD638
%
4
elongation
屈服
ISO527-2/50
%
4
elongation
断裂
ASTMD638
%
1
elongation
断裂
ISO527-2/50
%
9
Bending modulus
50.0mm跨距
ASTMD790
Mpa
2
Bending modulus
ISO178
Mpa
2
bending strength
屈服,50.0mm跨距
ASTMD790
Mpa
1
Bending strength 5,
ISO178
Mpa
9
Impact strength of cantilever beam gap
-30°C
ASTMD256
J/m
1
Impact strength of cantilever beam gap
23°C
ASTMD256
J/m
7
Impact strength of cantilever beam gap
-30°C9
ISO180/1A
kJ/m²
1
Impact strength of cantilever beam gap
-30°C10
ISO180/1A
kJ/m²
1
Impact strength of cantilever beam gap
23°C9
ISO180/1A
kJ/m²
2
Impact strength of cantilever beam gap
23°C10
ISO180/1A
kJ/m²
2
Dart impact equipped with measuring instruments
23°C,TotalEnergy
ASTMD3763
J
6
Thermal performance
Test Condition
Test Method
Unit
PC/ABS/SABIC INNOVATIVE NANSHA/CX7240-701
RTI Imp
UL746
°C
9
RTIElec
UL746
°C
9
RTIStr
UL746
°C
9
thermal conductivity
ISO8302
W/m/K
0
Hot deformation temperature
0.45MPa,未退火,3.20mm
ASTMD648
°C
1
Hot deformation temperature
1.8MPa,未退火,3.20mm
ASTMD648
°C
8
Hot deformation temperature
1.8MPa,未退火,6.40mm
ASTMD648
°C
9
Hot deformation temperature
1.8MPa,Unannealed,64.0mmSpan
ISO75-2/Af
°C
9
vicat softening point
ASTMD152512
°C
1
vicat softening point
--
ISO306/B50
°C
1
vicat softening point
--
ISO306/B120
°C
1
Linear coefficient of thermal expansion
MD：-40到40°C
ASTME831
cm/cm/°C
7
Linear coefficient of thermal expansion
MD：-40到40°C
ISO11359-2
cm/cm/°C
7
Linear coefficient of thermal expansion
TD：-40到40°C
ASTME831
cm/cm/°C
7
Linear coefficient of thermal expansion
TD：-40到40°C
ISO11359-2
cm/cm/°C
7
Electrical performance
Test Condition
Test Method
Unit
PC/ABS/SABIC INNOVATIVE NANSHA/CX7240-701
Surface resistivity
IEC60093
ohms
>
Dielectric strength
0.800mm,在油中
IEC60243-1
KV/mm
3
Dielectric strength
1.60mm,在油中
IEC60243-1
KV/mm
2
Dielectric strength
3.20mm,在油中
IEC60243-1
KV/mm
1
Volume resistivity
IEC60093
ohms·cm
>
flammability
Test Condition
Test Method
Unit
PC/ABS/SABIC INNOVATIVE NANSHA/CX7240-701
Extreme Oxygen Index
ISO4589-2
%
3
Hot filament ignition temperature
0.75mm13
IEC60695-2-13
°C
7
Hot filament ignition temperature
1.0mm
IEC60695-2-13
°C
8
Hot filament ignition temperature
1.5mm13
IEC60695-2-13
°C
7
Hot filament ignition temperature
3.0mm13
IEC60695-2-13
°C
7
Hot filament ignition temperature
3.0mm
IEC60695-2-13
°C
8
Burning wire flammability index
0.75mm13
IEC60695-2-12
°C
9
Burning wire flammability index
0.75mm
IEC60695-2-12
°C
9
Contact Us