ABS PC/ABS M130S MARPLEX AUSTRALIA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | MARPLEX AUSTRALIA/PC/ABS M130S |
---|---|---|---|
Impact strength of cantilever beam gap | 3.20mm | ASTM D256 | 630 J/m |
Dart impact | 3.20mm | ASTM D3029 | 55.0 J |
hardness | Test Condition | Test Method | MARPLEX AUSTRALIA/PC/ABS M130S |
---|---|---|---|
Rockwell hardness | R级 | ASTM D785 | 115 |
Mechanical properties | Test Condition | Test Method | MARPLEX AUSTRALIA/PC/ABS M130S |
---|---|---|---|
bending strength | 3.20mm | ASTM D790 | 85.0 MPa |
elongation | 断裂,3.20mm | ASTM D638 | 100 % |
tensile strength | 3.20mm | ASTM D638 | 55.0 MPa |
Flexural modulus | 3.20mm | ASTM D790 | 2400 MPa |
flammability | Test Condition | Test Method | MARPLEX AUSTRALIA/PC/ABS M130S |
---|---|---|---|
Hot filament ignition temperature | 1.6mm | AS/NZS60695.2.12 | 550 °C |
UL flame retardant rating | 1.6mm | UL 94 | HB |
physical property | Test Condition | Test Method | MARPLEX AUSTRALIA/PC/ABS M130S |
---|---|---|---|
Shrinkage rate | MD:3.00mm | ASTM D955 | 0.60 % |
Water absorption rate | 24hr | ASTM D570 | 0.25 % |
melt mass-flow rate | 250°C/3.8kg | ASTM D1238 | 12 g/10min |
density | ASTM D792 | 1.12 g/cm³ |
Thermal performance | Test Condition | Test Method | MARPLEX AUSTRALIA/PC/ABS M130S |
---|---|---|---|
Heat distortion temperature | 1.8MPa,未退火,6.40mm,HDT | ASTM D648 | 100 °C |
vicat | ASTM D15254 | 132 °C | |
Heat distortion temperature | 1.8MPa,未退火,12.7mm,HDT | ASTM D648 | 106 °C |
Linear coefficient of thermal expansion | MD | ASTM D696 | 7.2E-05 cm/cm/°C |
Heat distortion temperature | 1.8MPa,未退火,3.20mm,HDT | ASTM D648 | 98.0 °C |