Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PET FR530 DUPONT USA
Rynite®
Electrical field、Electronic field、Household appliances、Household appliances、Automotive sector
enhance、Glass fiber reinforced、wear resistant、High rigidity、High temperature resistan、Filler: Glass fiber reinf、30% filler by weight
UL
SGS
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT USA/FR530 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 10 kJ/m² |
| -30°C | ISO 179/1eA | 9.0 kJ/m² | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 40 kJ/m² |
| -30°C | ISO 179/1eU | 40 kJ/m² |
| Mechanical properties | Test Condition | Test Method | DUPONT USA/FR530 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 11500 Mpa | |
| Tensile creep modulus | 1hr | ISO 899-1 | 11200 Mpa |
| Tensile strain | 断裂 | ISO 527-2 | 2.0 % |
| Flexural modulus | ISO 178 | 10500 Mpa | |
| Tensile creep modulus | 1000hr | ISO 899-1 | 9700 Mpa |
| tensile strength | 断裂 | ISO 527-2 | 135 Mpa |
| Electrical performance | Test Condition | Test Method | DUPONT USA/FR530 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 3 | |
| dielectric strength | IEC 60243-1 | 39 KV/mm | |
| Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| Dissipation Factor | 100Hz | IEC 60250 | 7E-03 |
| relative permittivity | 100Hz | IEC 60250 | 4.80 |
| 1MHz | IEC 60250 | 4.30 | |
| Surface Resistivity | IEC 60093 | 1E+14 ohms | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 2 |
| Dissipation Factor | 1MHz | IEC 60250 | 0.013 |
| flammability | Test Condition | Test Method | DUPONT USA/FR530 |
|---|---|---|---|
| UL flame retardant rating | 0.35mm | UL 94 | V-0 |
| 0.35mm | IEC 60695-11-10,-20 | V-0 | |
| 1.5mm | IEC 60695-11-10,-20 | V-0 | |
| FMVSS flammability | FMVSS302 | DNI | |
| UL flame retardant rating | 1.5mm | UL 94 | V-0 |
| Limiting Oxygen Index | ISO 4589-2 | 33 % |
| physical property | Test Condition | Test Method | DUPONT USA/FR530 |
|---|---|---|---|
| Melt volume flow rate | 280°C/2.16kg | ISO 1133 | 6.00 cm3/10min |
| Shrinkage rate | TD | ISO 294-4 | 0.80 % |
| MD | ISO 294-4 | 0.20 % | |
| Water absorption rate | 饱和,23°C,2.00mm | ISO 62 | 0.75 % |
| Ejection Temperature | 170 °C | ||
| density | ISO 1183 | 1.68 g/cm³ | |
| Water absorption rate | 平衡,23°C,2.00mm,50%RH | ISO 62 | 0.15 % |
| Thermal performance | Test Condition | Test Method | DUPONT USA/FR530 |
|---|---|---|---|
| RTI Str | 0.75mm | UL 746 | 155 °C |
| RTI Imp | 1.5mm | UL 746 | 155 °C |
| vicat | ISO 306/B50 | 220 °C | |
| RTI Elec | 0.40mm | UL 746 | 155 °C |
| 3.0mm | UL 746 | 155 °C | |
| RTI Imp | 3.0mm | UL 746 | 155 °C |
| RTI Elec | 0.75mm | UL 746 | 155 °C |
| Linear coefficient of thermal expansion | TD：-- | ISO 11359-2 | 9.2E-05 cm/cm/°C |
| RTI Imp | 0.40mm | UL 746 | 155 °C |
| 0.75mm | UL 746 | 155 °C | |
| melting temperature | ISO 11357-3 | 252 °C | |
| Linear coefficient of thermal expansion | MD：-40to23°C | ISO 11359-2 | 2.2E-05 cm/cm/°C |
| TD：-40to23°C | ISO 11359-2 | 6.8E-05 cm/cm/°C | |
| MD：-- | ISO 11359-2 | 1.9E-05 cm/cm/°C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 243 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 225 °C | |
| RTI Str | 1.5mm | UL 746 | 155 °C |
| EffectiveThermalDiffusivity | UL 746 | 1.1E-07 m²/s | |
| 3.0mm | UL 746 | 155 °C | |
| RTI Elec | 1.5mm | UL 746 | 155 °C |
| RTI Str | 0.40mm | UL 746 | 155 °C |