Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS 3904 STYRON US
MAGNUM™
--
High impact resistance、High gloss
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | STYRON US/3904 |
|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/1eU2 | NoBreak |
| 23°C | ISO 179/1eU2 | NoBreak | |
| 23°C | ISO 179/1eA2 | 38.0 kJ/m² |
| Mechanical properties | Test Condition | Test Method | STYRON US/3904 |
|---|---|---|---|
| Tensile modulus | 3.20mm,注塑 | ISO 527-2 | 1820 Mpa |
| Tensile strain | 屈服 | ISO 527-22 | 2.5 % |
| Nominal fracture strain | ISO 527-22 | 45 % | |
| Flexural modulus | 3.20mm,InjectionMolded | ISO 178 | 1900 Mpa |
| bending strength | 3.20mm,InjectionMolded | ISO 178 | 58.0 Mpa |
| tensile strength | 屈服,3.20mm,注塑 | ISO 527-2/50 | 37.0 Mpa |
| Tensile strain | 屈服,3.20mm,注塑 | ISO 527-2/50 | 2.6 % |
| tensile strength | 屈服 | ISO 527-22 | 35.0 Mpa |
| Tensile strain | 屈服,3.20mm,注塑 | ISO 527-2/100 | 2.8 % |
| tensile strength | 屈服,3.20mm,注塑 | ISO 527-2/100 | 39.0 Mpa |
| Tensile modulus | ISO 527-22 | 1900 Mpa |
| Electrical performance | Test Condition | Test Method | STYRON US/3904 |
|---|---|---|---|
| Volume resistivity | IEC 600932 | >1.0E+13 ohms·m |
| flammability | Test Condition | Test Method | STYRON US/3904 |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | UL 94 | HB |
| burning rate | 2.00mm | ISO 3795 | 40 mm/min |
| Normal combustion performance with a thickness of 1.6mm | 1.50mm,UL | HB 4.21 | |
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| carbon emission | VDA277 | 20.0 µg/g |
| physical property | Test Condition | Test Method | STYRON US/3904 |
|---|---|---|---|
| Shrinkage rate | MD | ISO 294-4 | 0.40-0.70 % |
| Melt volume flow rate | 220°C/10.0kg | ASTM D1505 | 4.00 cm3/10min |
| Apparent density | ISO 60 | 0.65 g/cm³ | |
| Melt volume flow rate | 220°C/10.0kg | ISO 1133 | 4.70 cm3/10min |
| melt mass-flow rate | 220°C/10.0kg | ISO 1133 | 4.5 g/10min |
| Thermal performance | Test Condition | Test Method | STYRON US/3904 |
|---|---|---|---|
| vicat | 50N | ISO 3062 | 97.0 °C |
| Heat distortion temperature | 1.8MPa,退火，HDT | ISO 75-2/A | 97.0 °C |
| vicat | ISO 306/B50 | 97.0 °C | |
| Heat distortion temperature | 1.8MPa，HDT | ISO 75-22 | 97.0 °C |