PA66 RBL 2500 A SCHULMAN USA
SCHULAMID®
--
Filler: Glass fiber reinf、25% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | A SCHULMAN USA/RBL 2500 |
|---|---|---|---|
| Continuous Use Temperature | °C | 110到220 | |
| Melting temperature | °C | 260 | |
| Flow | mm/mm/°C | 142.2E-5到203.2E-5 | |
| 8.0Mpa, Unannealed | °C | 65到220 | |
| 1.8MPa, Unannealed | °C | 230到250 |
| Hardness | Test Condition | Test Method | A SCHULMAN USA/RBL 2500 |
|---|---|---|---|
| Ball Indentation Hardness | MPa | 222.76到370.34 |
| Physical | Test Condition | Test Method | A SCHULMAN USA/RBL 2500 |
|---|---|---|---|
| Modeling Shrinkage | 23℃ | % | 0.10到0.31 |
| Saturation ,23℃ | % | 3.5到5.0 | |
| Flow,23℃,50%RH | % | 1.2到1.5 |
| Mechanical Properties | Test Condition | Test Method | A SCHULMAN USA/RBL 2500 |
|---|---|---|---|
| Tensile Stress | 断裂,23℃ | MPa | 144.83到292.41 |
| Tensile Modulus | 23℃ | MPa | 8206.9到28000.0 |
| Tensile Strain | 断裂,23℃ | % | 1.9到3.1 |
| Other | Test Condition | Test Method | A SCHULMAN USA/RBL 2500 |
|---|---|---|---|
| purpose | 电工电子器材 | ||
| characteristic | PA 66为基础设计的化合物 |
| Impact Properties | Test Condition | Test Method | A SCHULMAN USA/RBL 2500 |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 23℃ | kJ/m² | 11.143到19.964 |
| Electrical Properties | Test Condition | Test Method | A SCHULMAN USA/RBL 2500 |
|---|---|---|---|
| Volume Resistivity | 23℃ | ohms·cm | 1.0E+12到1.0E+14 |
| Dielectric Strength | 23℃ | V/mil | 840 |