PA6 UNIPA® MLo Nytef Plastics, Ltd.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Nytef Plastics, Ltd./UNIPA® MLo |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256 | 85 J/m |
| hardness | Test Condition | Test Method | Nytef Plastics, Ltd./UNIPA® MLo |
|---|---|---|---|
| Rockwell hardness | M级 | ASTM D785 | 85 |
| R级 | ASTM D785 | 112 |
| Mechanical properties | Test Condition | Test Method | Nytef Plastics, Ltd./UNIPA® MLo |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 20to60 % |
| tensile strength | ASTM D638 | 68.9 MPa | |
| compressive strength | ASTM D695 | 86.2 MPa | |
| Tensile modulus | ASTM D638 | 2760 MPa | |
| Flexural modulus | ASTM D790 | 3100 MPa | |
| coefficient of friction | ASTM D1894 | 0.14 | |
| bending strength | ASTM D790 | 103 MPa |
| Electrical performance | Test Condition | Test Method | Nytef Plastics, Ltd./UNIPA® MLo |
|---|---|---|---|
| Dissipation Factor | 60Hz | ASTM D150 | 0.020 |
| Volume resistivity | ASTM D257 | >1.0E+13 ohms·cm | |
| dielectric strength | ASTM D149 | 16 kV/mm | |
| dielectric constant | 1MHz | ASTM D150 | 3.70 |
| flammability | Test Condition | Test Method | Nytef Plastics, Ltd./UNIPA® MLo |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| physical property | Test Condition | Test Method | Nytef Plastics, Ltd./UNIPA® MLo |
|---|---|---|---|
| Water absorption rate | 饱和 | ASTM D570 | 4.0 % |
| 24hr | ASTM D570 | 0.60 % | |
| density | ASTM D792 | 1.14 g/cm³ |
| Thermal performance | Test Condition | Test Method | Nytef Plastics, Ltd./UNIPA® MLo |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 93.3 °C |
| Continuous use temperature | 内部方法 | 98.9 °C | |
| Linear coefficient of thermal expansion | MD | ASTM D696 | 9E-05 cm/cm/°C |
| melting temperature | ASTM D3418 | 221 °C |