MMS -MAS MAS10, MAS10F 日本大赛璐
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | 日本大赛璐/-MAS MAS10, MAS10F |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 2.0 kJ/m² |
| Impact strength of cantilever beam gap | 23°C,6.40mm | ASTM D256 | 15 J/m |
| hardness | Test Condition | Test Method | 日本大赛璐/-MAS MAS10, MAS10F |
|---|---|---|---|
| Hardness (Rockwell) | M计秤 | ISO 2039-2 | 73 |
| Mechanical properties | Test Condition | Test Method | 日本大赛璐/-MAS MAS10, MAS10F |
|---|---|---|---|
| tensile strength | 屈服 | ISO 527-2 | 62.0 MPa |
| Flexural modulus | ISO 178 | 3300 MPa | |
| bending strength | ISO 178 | 105 MPa |
| flammability | Test Condition | Test Method | 日本大赛璐/-MAS MAS10, MAS10F |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| physical property | Test Condition | Test Method | 日本大赛璐/-MAS MAS10, MAS10F |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D955 | 0.30to0.50 % |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.11 % |
| density | ISO 1183 | 1.08 g/cm³ | |
| melt mass-flow rate | 220°C/10.0kg | ISO 1133 | 22 g/10min |
| Thermal performance | Test Condition | Test Method | 日本大赛璐/-MAS MAS10, MAS10F |
|---|---|---|---|
| BallPressure Test | 90 °C | ||
| Hot deformation temperature (HDT) | 1.8MPa,未退火，HDT | ISO 75-2/A | 77.0 °C |
| vicat | ISO 306/B50 | 90.0 °C | |
| MD | ISO 11359-2 | 7E-05 cm/cm/°C | |
| Hot deformation temperature (HDT) | 1.8MPa,未退火,12.7mm，HDT | ASTM D648 | 87.0 °C |