PC HF-1023IM PC vs. - Plastic Material Properties Comparison Chart at Plas.com

Material Selector

All

Plastic Materials Additives Masterbatch Material Selector Price Index Trade Data Plastic News About Us

Material Comparison

Add Comparison Model

Select Products for Comparison (1/4)

Highlight Differences

Hide Same

Product Name / Manufacturer / Model

Grade

Reference Price

PC Samsung Cheil South Korea HF-1023IM

Injection grade

US$ 3,240 / MT

FOB Guangzhou port, China

injection	Test Condition	Test Method	Samsung Cheil South Korea/HF-1023IM
Back pressure			0.981 to 2.94 Mpa
Temperature at the front of the material cylinder			290 °C
Spray nozzle temperature			300 °C
Screw speed			40 to 80 rpm
Mold temperature			80 to 100 °C
Injection pressure			98.1 Mpa
Hot air dryer			2.0 to 4.0 °C
Vacuum drying machine			4.0 to 6.0 °C
Temperature in the middle of the barrel			280 °C
Suggested maximum moisture content			< 0.020 %
Temperature at the rear of the barrel			270 °C
impact performance	Test Condition	Test Method	Samsung Cheil South Korea/HF-1023IM
Impact strength of cantilever beam gap	23°C, 3.18 mm	ASTM D256	690 J/m
Impact strength of cantilever beam gap		23°C6	ISO 180/1A	63 kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179/1eA	68 kJ/m²
Impact strength of cantilever beam gap	23°C, 6.35 mm	ASTM D256	540 J/m
thermal performance	Test Condition	Test Method	Samsung Cheil South Korea/HF-1023IM
Vicat softening temperature	--	ISO 306/B50	140 °C
Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm	ISO 75-2/A	120 °C
		1.8 MPa, Unannealed, 6.40 mm	ASTM D648	126 °C
		0.45 MPa, Unannealed, 4.00 mm	ISO 75-2/B	133 °C
		0.45 MPa, Annealed, 4.00 mm	ISO 75-2/B	130 °C
Vicat softening temperature	--	ISO 306/B120	142 °C
Hot deformation temperature	1.8 MPa, Annealed, 4.00 mm	ISO 75-2/A	120 °C
Physical properties	Test Condition	Test Method	Samsung Cheil South Korea/HF-1023IM
Water absorption rate	Saturation, 23°C	ASTM D570	0.35 %
Shrinkage rate	Flow : 3.20 mm	ASTM D955	0.44 - 0.53 %
Shrinkage rate		Flow : 2.00 mm	ISO 294-4	0.44 - 0.53 %
melt mass-flow rate	250°C/10.0 kg	ASTM D1238	22 g/10 min
density	本色	ASTM D792	1.18 g/cm³
Shrinkage rate	Across FlowFlow : 3.20 mm	ASTM D955	0.45 - 0.55 %
Shrinkage rate		横向Flow : 2.00 mm	ISO 294-4	0.45 - 0.55 %
mechanical properties	Test Condition	Test Method	Samsung Cheil South Korea/HF-1023IM
bending strength	--4	ASTM D790	83.0 Mpa
Bending modulus	--4	ASTM D790	2000 Mpa
elongation	Break3	ASTM D638	120 %
tensile strength	Break	ISO 527-2/50	96.0 Mpa
bending strength	--5	ISO 178	88.0 Mpa
tensile strength	Yield3	ASTM D638	59.0 Mpa
tensile strength		Yield	ISO 527-2/50	60.0 Mpa
Tensile modulus	--3	ASTM D638	1900 Mpa
Tensile modulus		--	ISO 527-2/50	2100 Mpa
Bending modulus	--5	ISO 178	2100 Mpa
elongation	Break	ISO 527-2/50	100 %
tensile strength	Break3	ASTM D638	69.0 Mpa
hardness	Test Condition	Test Method	Samsung Cheil South Korea/HF-1023IM
Rockwell hardness	R -Sale	ISO 2039-2	120
Rockwell hardness		R-Scale	ASTM D785	120