Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POP PL 1881G DOW THAILAND
AFFINITY™
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| film | Test Condition | Test Method | DOW THAILAND/PL 1881G |
|---|---|---|---|
| Blocking force | ASTM D3354-89 | 70 g | |
| Dart impact | 51µm | ASTM D1709B | >830 g |
| Elmendorf tear strength | TD:51µm | ASTM D1922 | 730 g |
| MD:51µm | ASTM D1922 | 560 g | |
| elongation | MD:断裂,51µm | ASTM D882 | 590 % |
| TD:断裂,51µm | ASTM D882 | 630 % | |
| film thickness | 51 µm | ||
| Initial sealing temperature | 51µm | 内部方法 | 85.0 °C |
| Secant modulus | 2%正割,TD:51µm | ASTM D882 | 96.9 Mpa |
| 2%正割,MD:51µm | ASTM D882 | 97.4 Mpa | |
| tensile strength | TD:断裂,51µm | ASTM D882 | 42.5 Mpa |
| TD:屈服,51µm | ASTM D882 | 7.17 Mpa | |
| MD:断裂,51µm | ASTM D882 | 45.4 Mpa | |
| MD:屈服,51µm | ASTM D882 | 8.07 Mpa | |
| Thin film puncture strength | 51µm | 内部方法 | 8.09 J |
| 51µm | 内部方法 | 82.3 N | |
| 51µm | 内部方法 | 21.9 J/cm³ |
| thermal performance | Test Condition | Test Method | DOW THAILAND/PL 1881G |
|---|---|---|---|
| melting temperature | 内部方法 | 100 °C | |
| vicat | ASTM D1525 | 86.0 °C |
| mechanical properties | Test Condition | Test Method | DOW THAILAND/PL 1881G |
|---|---|---|---|
| coefficient of friction | 与自身-动态 | ASTM D1894 | 0.15 |
| optical performance | Test Condition | Test Method | DOW THAILAND/PL 1881G |
|---|---|---|---|
| gloss | 20°,50.8µm | ASTM D2457 | 112 |
| Haze ratio | 50.8µm | ASTM D1003 | 3.2 % |
| transparency | 50.8µm | ASTM D1746 | 83.0 |
| Physical properties | Test Condition | Test Method | DOW THAILAND/PL 1881G |
|---|---|---|---|
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 1.0 g/10min |