HDPE EL-Lene™ H6007JU Thailand Siam Chemical
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Thailand Siam Chemical/EL-Lene™ H6007JU |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 34 J/m |
| hardness | Test Condition | Test Method | Thailand Siam Chemical/EL-Lene™ H6007JU |
|---|---|---|---|
| Shore hardness | 邵氏D | ASTM D2240 | 68 |
| Mechanical properties | Test Condition | Test Method | Thailand Siam Chemical/EL-Lene™ H6007JU |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | >650 % |
| tensile strength | 断裂 | ASTM D638 | 21.6 MPa |
| Flexural modulus | ASTM D790 | 1320 MPa | |
| tensile strength | 屈服 | ASTM D638 | 30.4 MPa |
| physical property | Test Condition | Test Method | Thailand Siam Chemical/EL-Lene™ H6007JU |
|---|---|---|---|
| density | ASTM D1505 | 0.964 g/cm³ | |
| Shrinkage rate | MD:2.00mm | ASTM D955 | 1.6 % |
| Environmental stress cracking resistance | 50°C,25%Igepal,模压成型,F50 | ASTM D1693B | 4.00 hr |
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 7.5 g/10min |
| Shrinkage rate | TD:2.00mm | ASTM D955 | 0.96 % |
| Thermal performance | Test Condition | Test Method | Thailand Siam Chemical/EL-Lene™ H6007JU |
|---|---|---|---|
| vicat | ASTM D1525 | 127 °C | |
| melting temperature | ASTM D2117 | 133 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ASTM D648 | 75.0 °C |
| brittle temperature | ASTM D746 | -60.0 °C |