Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
HDPE EQUATE PE EMDA-6200 EQUATE KUWAIT
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | EQUATE KUWAIT/EQUATE PE EMDA-6200 |
|---|---|---|---|
| DropImpactResistance-MeanFailureHeight | ASTM D2463 | 430.00 cm |
| Supplementary Information | Test Condition | Test Method | EQUATE KUWAIT/EQUATE PE EMDA-6200 |
|---|---|---|---|
| TopCrushingLoadatFailure | 23°C | ASTM D2659 | 50000 g |
| Mechanical properties | Test Condition | Test Method | EQUATE KUWAIT/EQUATE PE EMDA-6200 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 1100 % |
| Flexural modulus | ASTM D790 | 1250 MPa | |
| tensile strength | 屈服 | ASTM D638 | 27.0 MPa |
| physical property | Test Condition | Test Method | EQUATE KUWAIT/EQUATE PE EMDA-6200 |
|---|---|---|---|
| Environmental stress cracking resistance | F50 | ASTM D1693B | 50.0 hr |
| melt mass-flow rate | 190°C/21.6kg | ASTM D1238 | 29 g/10min |
| density | ASTM D792 | 0.954 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 0.40 g/10min |
| Thermal performance | Test Condition | Test Method | EQUATE KUWAIT/EQUATE PE EMDA-6200 |
|---|---|---|---|
| vicat | ASTM D1525 | 125 °C | |
| melting temperature | 内部方法 | 135 °C | |
| Crystallization peak temperature | DSC | 内部方法 | 112 °C |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ASTM D648 | 70.0 °C |
| brittle temperature | ASTM D746 | <-100 °C | |
| Linear coefficient of thermal expansion | MD | ASTM D696 | 1.2E-04 cm/cm/°C |