Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 A RV250AF 375 BK-PA1000B RADICI SUZHOU
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | RADICI SUZHOU/A RV250AF 375 BK-PA1000B |
|---|---|---|---|
| Tensile modulus | 1.0mm/min | ISO 527 | ISO 527 Mpa |
| Charpy Notched Impact Strength | 23℃ | ISO 179 | kJ/m² ISO 179 |
| “-”30℃1eA型 | ISO 179 | kJ/m² ISO 179 | |
| -30。0 | ISO 179 | kJ/m² ISO 179 | |
| bending strength | 2.0mm/min | ISO 178 | ISO 178 Mpa |
| Charpy Notched Impact Strength | 23°C1eA型 | ISO 179 | kJ/m² ISO 179 |
| elongation at break | 5mm/min | ISO 527 | ISO 527 % |
| Flexural modulus | 2.0mm/min | ISO 178 | ISO 178 Mpa |
| tensile strength | 5mm/min，断裂 | ISO 527 | ISO 527 Mpa |
| Electrical performance | Test Condition | Test Method | RADICI SUZHOU/A RV250AF 375 BK-PA1000B |
|---|---|---|---|
| Surface Resistivity | 500V | IEC 60093 | Ω IEC 60093 |
| CTI solution A | IEC 60112 | V IEC 60112 | |
| Volume resistivity | 500V | IEC 60093 | Ω.m IEC 60093 |
| physical property | Test Condition | Test Method | RADICI SUZHOU/A RV250AF 375 BK-PA1000B |
|---|---|---|---|
| Shrinkage rate | 垂直280℃ 60MPa模具温度:80℃ | ISO 294 | ISO 294 % |
| Water absorption rate | 23℃ 2.00mm在水里 | ISO 62 | ISO 62 % |
| 23℃ 50RH 2.00mm | ISO 62 | ISO 62 % | |
| Shrinkage rate | 流动280℃60MPa模具温度80℃ | ISO 294 | ISO 294 % |
| Thermal performance | Test Condition | Test Method | RADICI SUZHOU/A RV250AF 375 BK-PA1000B |
|---|---|---|---|
| Linear coefficient of thermal expansion | 23~55℃，垂直方向 | ISO 11359 | m/m/k ISO 11359 |
| melting temperature | 10℃/min | ISO 11357 | °C ISO 11357 |
| Linear coefficient of thermal expansion | 23~55℃，流动方向 | ISO 11359 | m/m/k ISO 11359 |
| vicat | 50℃/hr 50N | ISO 306 | °C ISO 306 |
| Heat distortion temperature | 1.8MPa，HDT | ISO 75 | °C ISO 75 |