Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
HDPE HDPE 3802-N REPSOL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Supplementary Information | Test Condition | Test Method | REPSOL/ HDPE 3802-N |
|---|---|---|---|
| Long-TermHydrostaticStrength | 20°C | ISO TR9080 | >8.00 MPa |
| hardness | Test Condition | Test Method | REPSOL/ HDPE 3802-N |
|---|---|---|---|
| Shore hardness | 邵氏D | ASTM D2240 | 60 |
| Electrical performance | Test Condition | Test Method | REPSOL/ HDPE 3802-N |
|---|---|---|---|
| dielectric constant | 1MHz | ASTM D1531 | 2.50 |
| Dissipation Factor | 1MHz | ASTM D1531 | 5E-03 |
| Mechanical properties | Test Condition | Test Method | REPSOL/ HDPE 3802-N |
|---|---|---|---|
| Internal pressure resistance | 4.6MPa:80°C | EN1555/12201 | >6.9 day |
| 10MPa:20°C | EN1555/12201 | >4.2 day | |
| 4.0MPa:80°C | EN1555/12201 | >41.7 day | |
| tensile strength | 断裂 | ISO 527-2 | 28.0to30.0 MPa |
| Tensile strain | 断裂 | ISO 527-2 | 800to900 % |
| Flexural modulus | ASTM D790 | 700 MPa |
| physical property | Test Condition | Test Method | REPSOL/ HDPE 3802-N |
|---|---|---|---|
| melt mass-flow rate | 190°C/5.0kg | ISO 1133 | 0.85 g/10min |
| density | 23°C | ISO 1183 | 0.948to0.949 g/cm³ |
| Environmental stress cracking resistance | F0 | ASTM D1693 | >1000 hr |
| Carbon black content | ASTM D1603 | 2.3 % | |
| Environmental stress cracking resistance | 10%Igepal,F50 | ASTM D1693 | >1000 hr |
| melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 0.18to0.20 g/10min |
| 190°C/21.6kg | ISO 1133 | 18 g/10min |
| aging | Test Condition | Test Method | REPSOL/ HDPE 3802-N |
|---|---|---|---|
| Retention of Mechanical Properties | 100°C | ISO 527-2 | >75 % |
| Thermal performance | Test Condition | Test Method | REPSOL/ HDPE 3802-N |
|---|---|---|---|
| Oxygen induction time | 200°C | EN728 | >30 min |
| 210°C | EN728 | >20 min | |
| brittle temperature | ASTM D746 | <-70.0 °C | |
| vicat | ISO 306/A | 126 °C |