ABS+PA RAMLLOY PVB702 POLYRAM ISRAEL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodPOLYRAM ISRAEL/RAMLLOY PVB702
Impact strength of cantilever beam gap23°CASTM D256750 J/m
23°CISO 18060 kJ/m²
Mechanical propertiesTest ConditionTest MethodPOLYRAM ISRAEL/RAMLLOY PVB702
elongation断裂ASTM D63830 %
Tensile strain断裂ISO 527-230 %
Flexural modulusASTM D7901480 MPa
Tensile modulusASTM D6381700 MPa
ISO 527-21700 MPa
tensile strength 屈服ASTM D63835.0 MPa
屈服ISO 527-235.0 MPa
Flexural modulusISO 1781480 MPa
bending strengthASTM D79060.0 MPa
ISO 17860.0 MPa
Electrical performanceTest ConditionTest MethodPOLYRAM ISRAEL/RAMLLOY PVB702
Volume resistivityIEC 600931E+15 ohms·cm
dielectric constant1MHzIEC 602503.00
Surface ResistivityIEC 600931E+14 ohms
flammabilityTest ConditionTest MethodPOLYRAM ISRAEL/RAMLLOY PVB702
UL flame retardant rating3.0mmUL 94HB
physical property Test ConditionTest MethodPOLYRAM ISRAEL/RAMLLOY PVB702
Shrinkage rateISO 25770.80to1.0 %
MDASTM D9550.80to1.0 %
Water absorption rate平衡,23°C,50%RHASTM D5701.4 %
melt mass-flow rate250°C/5.0kgISO 113320 g/10min
Water absorption rate平衡,23°C,50%RHISO 621.4 %
densityASTM D7921.06 g/cm³
ISO 11831.06 g/cm³
melt mass-flow rate250°C/5.0kgASTM D123820 g/10min
Thermal performanceTest ConditionTest MethodPOLYRAM ISRAEL/RAMLLOY PVB702
Heat distortion temperature1.8MPa,未退火，HDTASTM D64860.0 °C
0.45MPa,未退火，HDTASTM D64880.0 °C
0.45MPa,未退火，HDTISO 75-2/B80.0 °C
1.8MPa,未退火，HDTISO 75-2/A60.0 °C