PA+Olefin Lumid® HI5003A LG Chem Ltd.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LG Chem Ltd./Lumid® HI5003A |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C,6.40mm | ASTM D256 | 450 J/m |
| -30°C,6.40mm | ASTM D256 | 120 J/m |
| Mechanical properties | Test Condition | Test Method | LG Chem Ltd./Lumid® HI5003A |
|---|---|---|---|
| elongation | 断裂,3.20mm | ASTM D638 | 50 % |
| Flexural modulus | 6.40mm | ASTM D790 | 2060 MPa |
| bending strength | 屈服,6.40mm | ASTM D790 | 70.6 MPa |
| tensile strength | 屈服,3.20mm | ASTM D638 | 51.0 MPa |
| physical property | Test Condition | Test Method | LG Chem Ltd./Lumid® HI5003A |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | ASTM D955 | 1.4to1.5 % |
| melt mass-flow rate | 235°C/2.16kg | ASTM D1238 | 3.5 g/10min |
| Water absorption rate | 23°C,24hr | ASTM D570 | 0.50 % |
| density | ASTM D792 | 1.09 g/cm³ |
| Thermal performance | Test Condition | Test Method | LG Chem Ltd./Lumid® HI5003A |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火,6.40mm，HDT | ASTM D648 | 162 °C |