PC/PBT 1760-7100 SABIC INNOVATIVE JAPAN

XENOY™

Automotive External Parts

Chemical resistance,High mobility,Glass fiber reinforced,High impact resistance

--

--

--

--

--

--

--

--

--

--

--

--

--

--

--

Plastic Datasheets

thermal performance	Test Condition	Test Method	SABIC INNOVATIVE JAPAN/1760-7100
Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	125 °C
		1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span7	ISO 75-2/Af	101 °C
		1.8 MPa, Unannealed, 6.40 mm	ASTM D648	116 °C
Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	7.6E-5 cm/cm/°C
		Across Flow : -40°C	ISO 11359-2	7.6E-5 cm/cm/°C
		Flow : -40 to 40°C	ASTM E831	3.9E-5 cm/cm/°C
Vicat softening temperature	--	ASTM D15258	121 °C
		--	ISO 306/B120	130 °C
		--	ISO 306/B50	135 °C

mechanical properties	Test Condition	Test Method	SABIC INNOVATIVE JAPAN/1760-7100
Bending modulus	--4	ISO 178	4010 Mpa
Bending modulus		50.0 mm Span3	ASTM D790	3910 Mpa
bending strength	--4,5	ISO 178	133 Mpa
bending strength		Yield, 50.0 mm Span3	ASTM D790	131 Mpa
elongation	Break	ISO 527-2/5	3.0 %
		Yield2	ASTM D638	3.0 %
		Yield	ISO 527-2/5	3.0 %
		Break2	ASTM D638	3.0 %
Tensile modulus	--1	ASTM D638	5310 Mpa
Tensile modulus		--	ISO 527-2/1	4800 Mpa
tensile strength	Break	ISO 527-2/5	84.0 Mpa
		Yield	ISO 527-2/5	84.0 Mpa
		Break2	ASTM D638	84.0 Mpa
		Yield2	ASTM D638	84.0 Mpa

Physical properties	Test Condition	Test Method	SABIC INNOVATIVE JAPAN/1760-7100
melt mass-flow rate	250°C/5.0 kg	ASTM D1238	15 g/10 min
Melt Volume Flow Rate (MVR)	265°C/5.0 kg	ISO 1133	27.0 cm3/10min
Shrinkage rate	Across FlowFlow : 3.20 mm	Internal Method	0.40 - 0.60 %
Shrinkage rate		Flow : 3.20 mm	Internal Method	0.40 - 0.60 %
Water absorption rate	Saturation, 23°C	ISO 62	0.50 %
Water absorption rate		Equilibrium, 23°C, 50% RH	ISO 62	0.15 %

impact performance	Test Condition	Test Method	SABIC INNOVATIVE JAPAN/1760-7100
Dart impact	-30°C, Total Energy	ASTM D3763	3.00 J
		-30°C, Energy at Peak	ASTM D3763	3.00 J
		-20°C, Energy at Peak	ASTM D3763	4.00 J
		23°C, Total Energy	ASTM D3763	8.00 J

injection	Test Condition	Test Method	SABIC INNOVATIVE JAPAN/1760-7100
Back pressure			0.300 to 0.600 Mpa
drying temperature			110 °C
drying time			4.0 to 6.0 hr
Exhaust hole depth			0.013 to 0.020 mm
Mold temperature			65 to 95 °C
Processing (melt) temperature			260 to 280 °C
Screw speed			50 to 80 rpm
Spray nozzle temperature			255 to 275 °C
Suggested injection volume			50 to 80 %
Suggested maximum moisture content			0.020 %
Temperature at the front of the material cylinder			260 to 280 °C
Temperature at the rear of the barrel			250 to 270 °C
Temperature in the middle of the barrel			255 to 275 °C