PA66 S223-D DSM HOLAND
Akulon® 
Electrical field、Electronic field、Engine parts
Glass fiber reinforced、High rigidity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodDSM HOLAND/S223-D
Charpy Notched Impact Strength23°CISO 179/1eA6.0 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eU无断裂
Charpy Notched Impact Strength-30°CISO 179/1eA6.0 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/1eU无断裂
Mechanical propertiesTest ConditionTest MethodDSM HOLAND/S223-D
Tensile modulusISO 527-23600 Mpa
Nominal tensile fracture strainISO 527-210 %
bending strengthISO 178125 Mpa
Flexural modulusISO 1782800 Mpa
Tensile strain屈服ISO 527-24.0 %
tensile strength 屈服ISO 527-295.0 Mpa
Electrical performanceTest ConditionTest MethodDSM HOLAND/S223-D
relative permittivity100 HzIEC 602503.20
Dissipation Factor1 MHzIEC 602500.017
dielectric strengthIEC 60243-130 KV/mm
Volume resistivityIEC 600931.0E+15 ohms·cm
Dissipation Factor100 HzIEC 602506.0E-3
relative permittivity1 MHzIEC 602503.00
Surface ResistivityIEC 60093-- ohms
Compared to the Leakage Tracking Index (CTI)IEC 60112 V
physical property Test ConditionTest MethodDSM HOLAND/S223-D
Water absorption rate平衡, 23°C, 50% RHISO 622.3 %
densityISO 11831.14 g/cm³
Shrinkage rate流量ISO 294-40.95 %
Water absorption rate饱和, 23°CISO 628.5 %
Shrinkage rate横向流量ISO 294-40.95 %
Thermal performanceTest ConditionTest MethodDSM HOLAND/S223-D
melting temperatureISO 11357-3260 °C
Heat distortion temperature0.45 MPa, 未退火，HDTISO 75-2/B215 °C
1.8 MPa, 未退火，HDTISO 75-2/A85.0 °C
Linear coefficient of thermal expansion流动ISO 11359-21.0E-4 cm/cm/°C
横向ISO 11359-21.0E-4 cm/cm/°C