LLDPE Jam PE 16501 Jam Petrochemical Company
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Supplementary Information | Test Condition | Test Method | Jam Petrochemical Company/Jam PE 16501 |
|---|---|---|---|
| Inflation ratio (BUR) | 2.00to3.00 |
| film | Test Condition | Test Method | Jam Petrochemical Company/Jam PE 16501 |
|---|---|---|---|
| Dart impact | 25µm,吹塑薄膜 | ASTM D1709 | 110 g |
| Secant modulus | 2%正割,TD:25µm,吹塑薄膜 | ASTM D882 | 185 MPa |
| Elmendorf tear strength | TD:25µm,吹塑薄膜 | ASTM D1922 | 380 g |
| elongation | TD:断裂,25µm,吹塑薄膜 | ASTM D882 | 770 % |
| tensile strength | TD:屈服,25µm,吹塑薄膜 | ASTM D882 | 12.7 MPa |
| Elmendorf tear strength | MD:25µm,吹塑薄膜 | ASTM D1922 | 180 g |
| Secant modulus | 2%正割,MD:25µm,吹塑薄膜 | ASTM D882 | 160 MPa |
| tensile strength | TD:断裂,25µm,吹塑薄膜 | ASTM D882 | 33.0 MPa |
| film thickness | 12.0to60.0 µm | ||
| elongation | MD:断裂,25µm,吹塑薄膜 | ASTM D882 | 670 % |
| tensile strength | MD:屈服,25µm,吹塑薄膜 | ASTM D882 | 12.7 MPa |
| MD:断裂,25µm,吹塑薄膜 | ASTM D882 | 42.0 MPa |
| optical performance | Test Condition | Test Method | Jam Petrochemical Company/Jam PE 16501 |
|---|---|---|---|
| gloss | 45°,25.0µm,吹塑薄膜 | ASTM D2457 | 25 |
| Haze ratio | 25.0µm,吹塑薄膜 | ASTM D1003 | 35 % |
| physical property | Test Condition | Test Method | Jam Petrochemical Company/Jam PE 16501 |
|---|---|---|---|
| density | ASTM D1505 | 0.916 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 0.95 g/10min |