TPU-Ether Texin® 950LW Covestro - Polycarbonates
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | Covestro - Polycarbonates/Texin® 950LW |
|---|---|---|---|
| Shore hardness | 邵氏D | ASTM D2240 | 50 |
| 邵氏D | ISO 868 | 50 |
| Mechanical properties | Test Condition | Test Method | Covestro - Polycarbonates/Texin® 950LW |
|---|---|---|---|
| Taber abraser | 1000Cycles,1000g,H-18转轮 | ASTM D1044 | 75.0 mg |
| Flexural modulus | 23°C | ISO 178 | 114 MPa |
| 23°C | ASTM D790 | 114 MPa | |
| Taber abraser | 1000Cycles,1000g,H-18转轮 | ISO 4649 | 75.0 mg |
| elastomer | Test Condition | Test Method | Covestro - Polycarbonates/Texin® 950LW |
|---|---|---|---|
| elongation | 断裂 | ASTM D412 | 460 % |
| tensile strength | 100%应变 | ISO 37 | 14.5 MPa |
| 屈服 | ASTM D412 | 49.7 MPa | |
| compression set | 23°C,22hr | ISO 815 | 15 % |
| Shore hardness | ASTM D2632 | 35 % | |
| compression set | 70°C,22hr | ASTM D395B | 40 % |
| elongation | 断裂 | ISO 37 | 460 % |
| tensile strength | 屈服 | ISO 37 | 49.7 MPa |
| 300%应变 | ISO 37 | 30.3 MPa | |
| 300%应变 | ASTM D412 | 30.3 MPa | |
| compression set | 70°C,22hr | ISO 815 | 40 % |
| tear strength | ISO 34-1 | 130 kN/m | |
| tensile strength | 100%应变 | ASTM D412 | 14.5 MPa |
| compression set | 23°C,22hr | ASTM D395B | 15 % |
| tear strength | ASTM D624 | 131 kN/m |
| physical property | Test Condition | Test Method | Covestro - Polycarbonates/Texin® 950LW |
|---|---|---|---|
| Shrinkage rate | TD:2.54mm | ISO 2577 | 0.80 % |
| MD：2.54mm | ASTM D955 | 0.80 % | |
| MD:2.54mm | ISO 2577 | 0.80 % | |
| density | ASTM D792 | 1.15 g/cm³ | |
| ISO 1183 | 1.15 g/cm³ | ||
| Shrinkage rate | TD：2.54mm | ASTM D955 | 0.80 % |
| Thermal performance | Test Condition | Test Method | Covestro - Polycarbonates/Texin® 950LW |
|---|---|---|---|
| vicat | ASTM D15254 | 128 °C | |
| ISO 306/50 | 128 °C |