PCT CG933 BK010 CELANESE USA
THERMX®
Electronic and electrical、Automotive sector
Flame retardant、Glass fiber reinforced、Filler: Glass fiber reinf、30% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | CELANESE USA/CG933 BK010 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | 30 kJ/m² |
| Mechanical properties | Test Condition | Test Method | CELANESE USA/CG933 BK010 |
|---|---|---|---|
| Tensile modulus | ISO527-2/1A/1 | 10800 Mpa | |
| Flexural modulus | 23°C | ISO178 | 10000 Mpa |
| Bending stress | 23°C | ISO178 | 172 Mpa |
| Tensile strain | 断裂 | ISO527-2/1A/5 | 1.5 % |
| Tensile stress | 断裂 | ISO527-2/1A/5 | 114 Mpa |
| Rockwell hardness | M级 | ISO2039-2 | 119 |
| Electrical performance | Test Condition | Test Method | CELANESE USA/CG933 BK010 |
|---|---|---|---|
| CTI | IEC60112 | 440 V | |
| dielectric strength | IEC60243-1 | 33 KV/mm |
| flammability | Test Condition | Test Method | CELANESE USA/CG933 BK010 |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | V-0 |
| 0.8mm | UL94 | V-2 |
| physical property | Test Condition | Test Method | CELANESE USA/CG933 BK010 |
|---|---|---|---|
| Shrinkage rate | TD | ISO294-4 | 0.80 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO62 | 0.15 % |
| 饱和,23°C | ISO62 | 0.90 % | |
| Shrinkage rate | MD | ISO294-4 | 0.30 % |
| Thermal performance | Test Condition | Test Method | CELANESE USA/CG933 BK010 |
|---|---|---|---|
| TD | ISO11359-2 | 1E-04 cm/cm/°C | |
| 0.45MPa,未退火 | ISO75-2/B | 270 °C | |
| 1.8MPa,未退火 | ISO75-2/A | 250 °C | |
| melting temperature | ISO11357-3 | 285 °C | |
| MD | ISO11359-2 | 6E-06 cm/cm/°C |