PC PC-110L TAIWAN CHIMEI
WONDERLITE®
Automotive sector,Application in the automotive field
Weather resistance
MSDS
RoHS
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TAIWAN CHIMEI/PC-110L |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 75 kJ/m² |
| Impact strength of cantilever beam gap | 23°C,3.20mm | ASTM D256 | 850 J/m |
| 23°C | ISO 180/4A | 75 kJ/m² |
| hardness | Test Condition | Test Method | TAIWAN CHIMEI/PC-110L |
|---|---|---|---|
| Rockwell hardness | M级 | ASTM D785 | 77 |
| Mechanical properties | Test Condition | Test Method | TAIWAN CHIMEI/PC-110L |
|---|---|---|---|
| tensile strength | 屈服 | ISO 527-2/50 | 65.0 Mpa |
| elongation | 断裂 | ASTM D638 | 110 % |
| bending strength | ISO 178 | 90.0 Mpa | |
| Flexural modulus | ISO 178 | 2400 Mpa | |
| bending strength | ASTM D790 | 89.8 Mpa | |
| tensile strength | 屈服 | ASTM D638 | 61.6 Mpa |
| Tensile strain | 断裂 | ISO 527-2/50 | 120 % |
| Flexural modulus | ASTM D790 | 2340 Mpa | |
| tensile strength | 断裂 | ISO 527-2/50 | 75.0 Mpa |
| flammability | Test Condition | Test Method | TAIWAN CHIMEI/PC-110L |
|---|---|---|---|
| UL flame retardant rating | 2.5mm | UL 94 | V-2 |
| 1.5mm | UL 94 | V-2 |
| physical property | Test Condition | Test Method | TAIWAN CHIMEI/PC-110L |
|---|---|---|---|
| density | 比重 | ASTM D792 | 1.20 g/cm³ |
| 23°C | ISO 1183 | 1.20 g/cm³ | |
| Shrinkage rate | ISO 294-4 | 0.50-0.70 % | |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 10.0 cm3/10min |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 10 g/10min |
| Thermal performance | Test Condition | Test Method | TAIWAN CHIMEI/PC-110L |
|---|---|---|---|
| vicat | ASTM D15256 | 148 °C | |
| -- | ISO 306/A50 | 148 °C | |
| Heat distortion temperature | 1.8MPa,退火，HDT | ISO 75-2/A | 172 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 127 °C | |
| vicat | -- | ISO 306/B50 | 143 °C |
| Heat distortion temperature | 未退火，HDT | ASTM D648 | 125 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 6.0E-5to8.0E-5 cm/cm/°C |