PC/PET X2300-WX-YW50117 SABIC INNOVATIVE US
XYLEX™
Automotive Applications、Electronic and electrical
Flame retardant、High heat resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/X2300-WX-YW50117 |
|---|---|---|---|
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 48.6 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/X2300-WX-YW50117 |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 2410 Mpa | |
| elongation | 断裂 | ASTM D638 | 120 % |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 86.2 Mpa |
| elongation | 屈服 | ASTM D638 | 5.0 % |
| tensile strength | 断裂 | ASTM D638 | 44.8 Mpa |
| 屈服 | ASTM D638 | 58.6 Mpa | |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 2210 Mpa |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/X2300-WX-YW50117 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.80-1.0 % |
| melt mass-flow rate | 266°C/5.0kg | ASTM D1238 | 35 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/X2300-WX-YW50117 |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 7.2E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 127 °C |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 7.2E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 110 °C |