Mechanical properties	Test Condition	BASF GERMANY/B3WM602
Tensile creep modulus	1000h，湿	1250 Mpa
Charpy Notched Impact Strength	+23℃，干/湿	36/80 KJ/m
Impact Strength	+23℃，干/湿	8/15 J
Fracture stress (V=50mm/min)	干/湿	72/45 Mpa
Tensile modulus	干/湿	6600/3700 Mpa
Impact strength of cantilever beam gap	+23℃，干/湿	4.5/8.5 KJ/m
elongation	≤0.5%, +23℃，湿	1250 Mpa
ball-indentation hardness	干/湿	170/80 Mpa
Charpy Notched Impact Strength	30℃，干/湿	6 KJ/m
bending strength	干/湿	120/60 Mpa
Tensile yield stress (V=50mm/min)	干/湿	72/45 Mpa
elongation at break	干/湿，V=50mm/min	2.6/20 %

Electrical performance	Test Condition	BASF GERMANY/B3WM602
dielectric constant	1MHz，干/湿	3.5/6.2
Compared to the Leakage Traceability Index (CTI)	干/湿	CTI 550
dielectric strength	K20/P50，干/湿	105/80 KV/mm
loss angle	1MHz，干/湿	0.02/0.2
Surface Resistivity	干/湿	10 Ω
Volume resistivity	干/湿	10 Ω.cm

Thermal performance	Test Condition	BASF GERMANY/B3WM602
TEMPERATURE	在20000h/5000h，后拉伸强度下降50%时	110 °C
Heat distortion temperature	1.8MPa负荷，干态，HDT	150 °C
thermal conductivity	干态	0.36 W/(m.K)
maximum service temperature		180 °C
Linear coefficient of thermal expansion	（23-80）℃，干态	4-6.5/3.5-4.5
Heat distortion temperature	0.45MPa负荷,干态，HDT	200 °C
specific heat	干态	1.3 J/(g.K)